Investigation into the Hot-Forming Limit for 22MnB5 Hot-Forming Steel under a Stamping Process

Wenwu He,Bin Yang,Xuezhong Zhang,Min Li,Shuli Sun,Bao Wang,Qingxian Ma

DOI: https://doi.org/10.3390/met14050561

IF: 2.695

2024-05-11

Metals

Abstract:Hot-forming technology for 22MnB5 hot-forming steel (22MnB5 HF steel) plates has been widely used in the automobile manufacturing industry in recent years. Physical simulation and numerical modeling were carried out in order to determine the forming limit of a 22MnB5 steel plate for the stamping process. The deformation experiments were performed in a temperature range of 600~900 °C and a strain rate range of 0.1~10 s−1. In the uniaxial tensile tests, it was found that at the forming temperature of 600 °C, the condition of dynamic recrystallization was not fully reached, and thus the corresponding tensile strength was much larger than that at other deformation temperatures. In the numerical simulation of bulging experiments, it was found that 22MnB5 steel had good formability when the initial deformation temperature was high and the forming speed was low by using the instability criterion, combining the maximum punch force and strain path transition. The forming limit diagram of 22MnB5 steel at a temperature of 700 °C and tool speed of 25 mm/s was obtained by means of simulation and a hot stamping experiment. The establishment of the forming limit of the 22MnB5 steel plate can provide theoretical and technical guidance for the hot-forming process.

materials science, multidisciplinary,metallurgy & metallurgical engineering

What problem does this paper attempt to address?

### Problems the Paper Attempts to Solve

This paper primarily investigates the hot forming limits of 22MnB5 hot forming steel (22MnB5 HF steel) during the stamping process. Specifically, the paper aims to determine the forming limits of 22MnB5 steel sheets during the stamping process through physical simulation and numerical modeling, and to analyze the changes in material properties under different deformation conditions.

#### Main Research Content:
1. **Experimental Design**: Uniaxial tensile tests were conducted with a temperature range of 600 to 900°C and a strain rate range of 0.1 to 10 s⁻¹.
2. **Numerical Simulation**: Numerical simulations were performed using instability criteria combined with maximum punch force and strain path transformation to obtain the forming performance of 22MnB5 steel under different initial deformation temperatures and forming speeds.
3. **Experimental Verification**: A forming limit diagram of 22MnB5 steel at 700°C and a tool speed of 25 mm/s was established through hot stamping experiments.

#### Research Background:
With the development of the automotive manufacturing industry, higher demands are placed on material resources and environmental protection. 22MnB5 hot forming steel, with its high strength and excellent crash performance, can reduce vehicle weight by about 30%, making it one of the preferred materials for automotive structural components. However, when stamping at room temperature, this material is prone to issues such as wrinkling and cracking. Therefore, studying its hot forming technology to avoid these defects becomes particularly important.

#### Objectives:
- Establish the forming limits of 22MnB5 steel sheets at high temperatures to provide theoretical and technical guidance for the hot forming process.
- Analyze the plastic behavior of the material under different deformation conditions and predict the fracture behavior of the material.