ISIJ International, Vol. 47 (2007), No. 9, pp. 1239–1244

L. Wen,C. Bai,Shengfu Zhang,G. Qiu,Dengfu Chen

2007-01-01

Abstract:Microwave heating makes utilization of thermal effect produced by energy consumption of high-frequency electromagnetic waves in the interior of substance. Because electrical conductivity and loss factor of substance have close relationship with microwave frequency, temperature, composition, structure and impurity content of the substance, the characteristic of microwave heating have strong selectivity to promote some chemical reactions. The results indicated that TiO2 in the CaTiO3 accounts for 75–84% or so of the whole BF slag bearing titanium in Panzhihua steel Corp. Therefore, the focus of this research is to change current existing state of CaTiO3 in BF slag bearing titanium. That is to say, through alteration of slag components and cooling speed, to seek the condition that crystal granularity and crystallized quantities of CaTiO3 will become bigger, and to treat by microwave heating, all of which helps to separate CaTiO3 from BF slag bearing titanium. The distribution of CaTiO3, whose average diameter is only 41 mm in BF slag bearing titanium, appears to be thin and dispersive, so the research on relative magnetic susceptibility of CaTiO3 and other minerals in slag as well as effective fragmentation method or method of accelerating crystal grains to grow up is necessarily needed. From the perspective of fragmentation, due to low utilization ratio for traditional fragmentation method and hard property of slag bearing titanium which will consume a mass of energy if it is broken into 40 mm in diameter, so some other approaches have to be sought from viewpoint of economic benefits such as slag broken by microwave. The main petrographic minerals in BF slag bearing titanium are various such as CaTiO3, titanaugite, spinel, and so on, all of which have different loss factor, so their absorption ability for microwave is different as well as their heat expansion in which condition heat stress is produced in slag bearing titanium correspondingly. Therefore, as temperature rising rate and temperature reaching a fixed value, it’s theoretically analyzed that crystal grains of CaTiO3 or around them should be made to produce cracks, which will be of benefit to subsequent grinding of BF slag bearing titanium and development of separation technology for CaTiO3.