Abstract:In the process of promoting the commercialization of proton exchange membrane fuel cells, the long-term durability of the fuel cell has become a key consideration. While existing durability tests are critical for assessing cell performance, they are often time-consuming and do not quickly reflect the impact of actual operating conditions on the cell. In this study, improved testing protocols were utilized to solve this problem, which is designed to shorten the testing cycle and evaluate the degradation of the cell performance under real operating conditions more efficiently. Accelerated durability analysis for evaluating the MEA lifetime and performance decay process was carried out through two testing protocols—open circuit voltage (OCV)-based accelerated durability testing (ADT) and relative humidity (RH) cycling-based ADT. OCV-based ADT revealed that degradation owes to a combined mechanical and chemical process. RH cycling-based ADT shows that degradation comes from a mainly mechanical process. In situ fluoride release rate technology was employed to elucidate the degradation of the proton exchange membrane during the ADT. It was found that the proton exchange membrane suffered more serious damage under OCV-based ADT. The loss of F- after the durability test was up to 3.50 × 10−4 mol/L, which was 4.3 times that of the RH cycling-based ADT. In addition, the RH cycling-based ADT had a significant effect on the catalyst layer, and the electrochemically active surface area decreased by 48.6% at the end of the ADT. Moreover, it was observed that the agglomeration of the catalysts was more obvious than that of OCV-based ADT by transmission electron microscopy. It is worth noting that both testing protocols have no obvious influence on the gas diffusion layer, and the contact angle of gas diffusion layers does not change significantly. These findings contribute to understanding the degradation behavior of proton exchange membrane fuel cells under different working conditions, and also provide a scientific basis for developing more effective testing protocols.

Failure Behavior of Gas Diffusion Layer in Proton Exchange Membrane Fuel Cells

Failure of Cathode Gas Diffusion Layer in 1 Kw Fuel Cell Stack under New European Driving Cycle

Property Evolution of Gas Diffusion Layer and Performance Shrink of Fuel Cell During Operation

Power Evolution of Fuel Cell Stack Driven by Anode Gas Diffusion Layer Degradation

Recent Progress of the Gas Diffusion Layer in Proton Exchange Membrane Fuel Cells: Material and Structure Designs of Microporous Layer

Degradation mechanism analysis of substrate and microporous layer of gas diffusion layer in proton exchange membrane fuel cell

Proton exchange membrane fuel cell degradation under close to open-circuit conditions

Experimental Study on the Effect of Flow Channel Parameters on the Durability of PEMFC Stack and Analysis of Hydrogen Crossover Mechanism

Low Temperature Durability and Consistency Analysis of Proton Exchange Membrane Fuel Cell Stack Based on Comprehensive Characterizations

A Super Uniform Hydrophobic Gas Diffusion Layer for a Proton Exchange Membrane Fuel Cell

Enhancing the Dynamic Performance of Proton Exchange Membrane Fuel Cells Through Two-Phase Flow Experimental Investigation

Degradation Analysis of the Core Components of Metal Plate Proton Exchange Membrane Fuel Cell Stack under Dynamic Load Cycles

Structural Design of Microporous Layer to Mitigate Carbon Corrosion in Proton Exchange Membrane Fuel Cells

Degradation Differences of a Single Proton Exchange Membrane Fuel Cell: Energy Management Strategy and Dynamic Programming

Decomposition on the Degradation Mechanism of the Cathode Catalyst Layer under 1000 H of On-Road Heavy-Duty Transportation

Mass transfer capacity degradation of gas diffusion layer under 1000 hours real-world heavy duty load cycles

Study on Gas Diffusion Layer Durability of PEM Fuel Cell

Key Components Degradation in Proton Exchange Membrane Fuel Cells: Unraveling Mechanisms through Accelerated Durability Testing

Electrical resistance and microstructure of typical gas diffusion layers for proton exchange membrane fuel cell under compression

Degradation Effect of Gas Diffusion Layer on Water Transport in Polymer Electrolyte Membrane Fuel Cell

Performance degradation and process engineering of the 10 kW proton exchange membrane fuel cell stack