Cu 2 O/CuO heterojunction formed by thermal oxidation and decorated with Pt co-catalyst as an efficient photocathode for photoelectrochemical water splitting

Pan Wang,Zhifeng Liu,Changcun Han,Xinguo Ma,Zhengfu Tong,Baohua Tan
DOI: https://doi.org/10.1007/s11051-021-05383-2
IF: 2.533
2021-01-01
Journal of Nanoparticle Research
Abstract:Cuprous oxide (Cu 2 O) is a highly efficient p-type semiconductor, which has an appropriate band gap and favorable energy band positions, making it ideal to be considered as a photocathode material for photoelectrochemical (PEC) water splitting. However, the theoretical efficiency of Cu 2 O is still unachievable in practical situations due to the low separation rate of photogenerated electron–hole pairs. In this work, the surface of the Cu 2 O film was directly converted to CuO by thermal oxidation to form a Cu 2 O/CuO heterojunction with fewer defects at the interface. The PEC tests suggest that the Cu 2 O/CuO photocathode exhibits a photocurrent density of − 1.99 mA/cm 2 at 0 V vs. RHE benefit by the heterojunction with a good interface for efficient charge separation and transfer, which is 3.3 times higher than Cu 2 O (− 0.6 mA/cm 2 ). Furthermore, the performance of Cu 2 O/CuO can be greatly enhanced by depositing a Pt co-catalyst layer. The photocurrent density of Cu 2 O/CuO/Pt composites was 4.6 times higher than pristine Cu 2 O. More exciting, the stability of Cu 2 O with the CuO and Pt co-catalyst only presents a decline of 20% under illumination for 3600 s. This work points to the effective means of thermal oxidation that can form a heterojunction with relatively fewer interface defects and provides a strategy for the performance improvement of Cu 2 O photocathode in PEC water reduction.
What problem does this paper attempt to address?