Microstructure and performance characterization of in-situ Co2FeO4 whiskers reinforced YIG/YIG joints

Qianqian Chen,Panpan Lin,Xuanyu Du,Wumo Du,Tiesong Lin,Peng He

DOI: https://doi.org/10.1016/j.matchar.2021.111323

IF: 4.537

2021-01-01

Materials Characterization

Abstract:Bismuth-based glasses doped with different CoO contents were designed to realize the in-situ growth of Co2FeO4 whiskers in YIG/YIG joint. The microstructure, mechanical and dielectric properties of the joints were systematically investigated. The optimized processing joint with 23 mol% CoO doping, brazed at 725 °C for 15 min, under bonding pressure of 6 kPa was achieved. And the shear strength of joint reached a maximum of 72 MPa, which is attributed to the increased number and optimized spatial distribution of Co2FeO4 whiskers. The in-situ Co2FeO4 whiskers acted as effective hard phases in the glass matrix. The shear strength of YIG/YIG joint was enhanced by the crack propagation deflection and pulling out result from Co2FeO4 whiskers. The dielectric constant of YIG joints decreased from 16.2 to 15.3 at the frequency of 10 MHz, which is closer to that of the original YIG material with the CoO doping increasing. The dielectric loss tangent increased slightly with the growth of Co2FeO4 whiskers due to the hole hopping between Co3+⇔Co2+ ions. The effective bonding of YIG materials has broad application prospects for the integration of ferrite microwave devices.