Abstract:The effects of temperature on the tribological and dynamic mechanical properties (DMP) of aromatic liquid-crystal poly(ester-co-amide) were investigated. Specimens for the DMA test and friction and wear test were prepared by compression molding at elevated temperature. The dynamic mechanical properties of the resulting compression-molded liquid crystal polymer (LCP) specimens were evaluated on a Perkin-Elmer DMA instrument, in a three-point bending mode, at a heating rate of 10°C/min and frequency of 1Hz from room temperature to 250°C. The friction and wear behavior of the compression-molded LCP specimens sliding against SA52100 steel in a ball-on-disk configuration was evaluated on a high-temperature friction and wear tester from 25 to 300°C. The worn surface morphologies of the compression-molded LCP specimens were observed on a scanning electron microscope. It was found that the tribological and dynamic mechanical properties of the LCP strongly depended on the test temperature. Namely, the friction coefficients decreased significantly and the wear rate increased considerably with increasing temperature. This was attributed to the enhanced softening and plastic deformation of the LCP at elevated temperature. The LCP experienced severe plastic deformation, flowing and local melting owing to the destruction of the stiff backbones of the polymeric molecules at excessively high temperature, thus the largest wear rate of the tested LCP was generated at 300°C. Such a trend in the friction and wear behavior of the compression-molded LCP with temperature conformed well to the corresponding worn surface morphologies. Namely, the LCP worn surface was characterized by mild plastic deformation and micro-cracking as the LCP disk slid against the steel ball at 50°C, whilst at 100°C, the plastic deformation and adhesion became severe and the micro-cracking disappeared owing to the plastic flow. The plastic deformation and adhesion became increasingly more severe with further increase of the test temperature up to 150, 200, and 250°C, owing to the increased plastic flow and local softening and melting of the LCP. Moreover, the storage modulus of the compression-molded LCP greatly decreased with increasing temperature, as did the loss modulus, while the complex modulus and tan δ increased with increasing temperature, which agreed well with the corresponding trend of the tribological behavior with temperature. It was confirmed that the dynamic mechanical properties of the polymer were an important factor of the high temperature tribological behavior.

Temperature-controlled Friction Coefficient Lubricated by Liquid Crystal

Effect of Temperature on the Tribological and Dynamic Mechanical Properties of Liquid Crystalline Polymer

Effect of Liquid Crystal Molecular Orientation Controlled by an Electric Field on Friction

Preliminary study of the superlubricity behavior of ZrO2/PI lubricating with liquid crystal

Research on the antifriction mechanism of liquid crystal additives (LCA)

Toward Low Friction in High Vacuum by Designing Textured A-C/il Duplex Lubricating Film

Nano-tribological Properties and Mechanisms of the Liquid Crystal As an Additive

Friction Anisotropy Induced by Oriented Liquid Crystal Molecules

Friction-induced Lubricating Nanocoatings of Main-Chain Thermotropic Liquid Crystalline Polymer

Insight Into The Superlubricity And Self-Assembly Of Liquid Crystals

Ordering of the 7cb Liquid Crystal Induced by Nanoscale Confinement and Boundary Lubrication

Study on ultra-low friction performance of PTFE film combined with water-based ionic liquid lubrication at electrical contact interfaces

On-Line Feedback Control of Sliding Friction of Metals Lubricated by Adsorbed Boundary SDS Films

In Situ Observation Of The Molecular Ordering In The Lubricating Point Contact Area

Investigation of the liquid crystal additive's influence on film formation in nano scale

Anti-Electroviscous Effect of Near-Surface 5cb Liquid Crystal and Its Boundary Lubrication Property

Friction-induced Surface Textures of Liquid Crystalline Polymer Evaluated by Atomic Force Microscopy, Spectroscopy and Nanoindentation

Molecular Behaviors in Thin Film Lubrication—part One: Film Formation for Different Polarities of Molecules

Investigation of the Running-in Process and Friction Coefficient under the Lubrication of Ionic Liquid/water Mixture

An Experimental Study on Voltage-Controlled Friction of Alumina/Brass Couples in Zinc Stearate/Water Suspension

Mechanochemical in-situ construction of ionic liquid-functionalized covalent organic frameworks for anti-wear and friction reduction