Temperature-Dependent Magnetization Dynamics in Nanoscale Cu(tCu)/[Co/Ni]N Perpendicular Multilayers: Implications for Spintronic Applications

Guanjie Wu,Yang Ren,Qingyuan Jin,Zongzhi Zhang

DOI: https://doi.org/10.1021/acsanm.0c02662

IF: 6.14

2020-01-01

ACS Applied Nano Materials

Abstract:Magnetic multilayers with perpendicular magnetic anisotropy (PMA) have significant advantages in the development of spintronic applications. However, currently, the research on the temperature (T) dependence of magnetization dynamics is mainly focused on the in-plane magnetized ferromagnetic materials. In this work, the magnetic properties of the effective PMA field H-keff and intrinsic magnetic damping factor alpha(0) were investigated at various T for the nanoscale Cu(t(cu))/[Co/Ni](N) perpendicular multilayers by the time-resolved magneto-optical Kerr effect approach. It is quite remarkable that both the H-keff and alpha(0) exhibit a peak value at T similar to 180 K for thin films of N = 2 and 5. The nonmonotonic variation of H-keff is resulting from the competition between the increased PMA constant K-u and saturation magnetization at low T, while the variation of alpha(0) is caused by the coeffect of increased K-u and reduced two-magnon scattering that mainly arises from spin fluctuations in the magnetic dead layer (MDL) at the Cu/Co interface. In contrast, for the sample of N = 8 with a thick enough magnetic layer, K-u plays a dominant role in the observed variation behaviors within our measurement temperature range, resulting in a monotonically increased H-keff and alpha(0) with the decrease in T. Our results reveal that the magnetization dynamics are highly sensitive to the interfacial MDL at low T, which is of significance for the applications of practical spintronic devices with ultrafast control of information operation.