Temperature‐Dependent Spin–Orbit Torques in Perpendicular Magnetic [co/ni]n/tbco Composite Films
Hongwei Xue,Shaohai Chen,Di Wu,Weihua Zhu,Yuanyuan Zhang,Chungang Duan,Jingsheng Chen,Qingyuan Jin,Zongzhi Zhang
DOI: https://doi.org/10.1002/aelm.201900014
IF: 6.2
2019-01-01
Advanced Electronic Materials
Abstract:The temperature (T) dependence of spin-orbit torque (SOT) efficiencies and magnetic properties are investigated in antiferromagnetically coupled Ta/Cu/[Co/Ni](N)/TbCo perpendicular composite films. By changing the Co/Ni repetition number N, the magnetization compensation temperature T-M can be widely modulated, decreasing from 295 K for N = 0 to below 10 K for N = 2. From temperature-dependent harmonic Hall measurements, it is shown that damping-like SOT field per current density chi(DL) = H-DL/J(ac) varies in a similar way to the net saturation magnetization M-S and reaches a maximum at T = T-M, whereas field-like H-FL/J(ac) is nearly independent with T. The observed slight deviation between chi(DL) and 1/M-S versus T curves at reduced temperatures is attributed to the increased spin Hall angle and interfacial spin transparency. It is found that the SOT efficiency xi varies from -0.04 to -0.06 and even to -0.13 for N = 0, 1 and 2, respectively, suggesting xi is intensively dependent on the details of the Ta/ferromagnet (FM) interface and the FM layer material. These results provide more insight into the SOT effects for exchange-coupled perpendicular composite structures, which are valuable for developing high-performance SOT devices.