Abstract:Laminate composites contain holes as a means of connection in industrial applications. A better understanding of the mechanical properties of open-hole components is necessary. Herein, progressive damage postbuckling analysis models are proposed for investigation of tensile damage and compressive buckling behaviors of open-hole laminate composites. The progressive damage model is based on failure criteria provided by the continuum damage mechanics model; virtual crack closure technology was employed to calculate the energy release rate for crack delamination in compressive postbuckling analysis. The models were utilized to analyze variations in the tensile and compressive mechanical properties, failure process, and buckling evolution of open-hole laminate composites using finite element analysis. The tensile failure patterns and failure processes of plies with different open-hole laminate composite angles were obtained and analyzed. Buckling characteristics, as well as the progression of buckling onset, buckling propagation, crack delamination, unstable delamination, and global buckling, were investigated. The influence of delamination crack length and crack distribution on the buckling properties of open-hole laminate composites are discussed in detail. Additionally, unstable and stable buckling characteristics were examined. The numerical results were in good agreement with theoretical and experimental results; damage initiated at the edge of a hole propagated to two sides with the onset of matrix damage, followed by fiber damage. The fiber damage of a 0°-ply led ultimately to laminate failure. The laminate with a symmetrical crack distribution showed stable buckling, whereas a short, nonsymmetrical distribution of cracks usually led to unstable buckling and delamination.

Progressive Failure Analysis of Composite Laminates Including Shear Nonlinearity

Continuum Damage Modeling and Progressive Failure Analysis of Carbon Fiber/epoxy Composite Pressure Vessel

Numerical Modeling of Shear Nonlinearity and Failure Analysis for Composite Laminates

Damage Analysis of Composite Laminate with Large Open-hole under Compression Using 3D Strain Progressive Damage Theory

A Progressive Damage Model of Composite Laminates under Low-Velocity Impact

Progressive failure analysis of perforated composite laminates considering nonlinear shear effect

Finite Element Analysis of a Modified Progressive Damage Model for Composite Laminates under Low-Velocity Impact

The Failure Analysis of Composite Bolted Joint Structure Based on a Nonlinear Model

Failure Analysis of Notched Composite Laminate with 3D Continuum Damage Mechanics

An Effective Progressive Damage Analysis Method for Failure Analysis of Composite Scarf Joint

Tensile Progressive Damage and Compressive Postbuckling Analysis of Open-Hole Laminate Composites

A Nonlinear Fatigue Damage Model for Life Prediction of Composite Laminates

Progressive Damage Simulation of Scaling Effects on Open-Hole Composite Laminates under Compression

Physically based failure analysis method for laminated composites

A nonlinear analytical model for tensile failure prediction of pseudo-ductile composite laminates

Progressive Damage Based Failure Analysis of Open-hole Composite Laminates under Tension

Numerical Investigation on the Repeated Low-Velocity Impact Behavior of Composite Laminates

Nonlinear progressive failure analysis of thick composite laminate under biaxial load

Progressive Failure Simulation for Damaged Composite Laminates Using Nonlinear Finite Element Method

Progressive Damage Simulation of Open-Hole Composite Laminates under Compression Based on Different Failure Criteria

Continuum damage mechanics based failure prediction and damage assessment in laminated composite structures