Understanding the High-Temperature Fatigue Crack Growth from Exceptional Nano-α Phases and {10$$ \bar{1} $$2} Deformation Twins in Hot Deformed Titanium Alloy

Wang Xiaoyan,Han Yuanfei,Su Xin,Li Shaopeng,Huang Guangfa,Mao Jianwei,Lu Weijie

DOI: https://doi.org/10.1007/s11661-021-06141-8

2021-01-01

Metallurgical and Materials Transactions A

Abstract:In this study, the fatigue crack growth rate (FCGR) of Ti-6Al-4V alloy at 723 K was measured by direct current potential drop (DCPD) method, and exceptional nano-α phases and {10 $$ \bar{1} $$ 2} deformation twins were newly found at the crack tip in Ti-6Al-4V alloy. The results showed that nano-α phases have Burgers orientation relationships (OR) (0001)α//(110)β, [ $$ \bar{2} $$ 110]α//[ $$ \bar{1} $$ 11]β with β phases. The terraced-structure interface consisted of (0 $$ \bar{1} $$ 10)α//(1 $$ \bar{1} $$ 2)β and (10 $$ \bar{1} $$ 0)α//(1 $$ \bar{1} $$ 0)β. Numerous dislocations accumulated in the β phase and became the diffused channels of O and V atoms. The α stabilizers (O element) diffused into the crystal lattice and β stabilizers (V element) spread out of the crystal lattice which accelerated the nano-α phases nucleation. and dislocations piled up at the primary α grain, interface and low angle grain boundaries (LAGBs), and dissociated into twinning dislocations to promote the twin nucleation. Dislocation transformation enabled nano-twins to grow through the primary α/β interface and strain transfer led that deformation twins nucleated in the adjacent primary α grains. With the effects of nano-α phases, LAGBs and twins, the resistance of crack propagation increased and the driving force decreased, and resulted in the low FCGR.