Effect of Α Phase on Fatigue Crack Growth of Ti-6242 Alloy

Hang-wei Zhou,Hui-qun Liu,Dan-qing Yi,Yu Xiao,Xiao-long Zhao,Jian Wang,Qi Gao
DOI: https://doi.org/10.1016/s1006-706x(17)30121-8
2017-01-01
Abstract:Fatigue crack growth as a function of a phase volume fraction in Ti-6Al-2Sn-4Zr-2Mo (Ti-6242) alloy was investigated using fatigue testing, optical microscopy, scanning electron microscopy, and transmission electron microscopy. The α + β annealing treatments with different solid solution temperatures and cooling rates were conducted in order to tailor microstructure with different a phase features in the Ti-6242 alloy, and fatigue crack growth mechanism was discussed after detailed microstructure characterization. The results showed that fatigue crack growth rate of Ti-6242 alloy decreased with the decrease in volume fraction of the primary a phase ( α p ). Samples with a large-sized α grain micro-structure treated at high solid solution temperature and slow cooling rate have lower fatigue crack growth rate. The appearance of secondary a phase ( α s ) with the increase of solid solution temperature led to crack deflection. Moreover, a fatigue crack growth transition phenomenon was observed in the Paris regime of Ti-6242 alloy with 29.8% α p (typical bi-modal microstructure) and large-sized a grain microstructure, owing to the change of fatigue crack growth mechanism.
What problem does this paper attempt to address?