Fracture Properties of Slag-Based Alkali-Activated Seawater Coral Aggregate Concrete
Bai Zhang,Hong Zhu,Fei Lu
DOI: https://doi.org/10.1016/j.tafmec.2021.103071
IF: 4.374
2021-01-01
Theoretical and Applied Fracture Mechanics
Abstract:The development of cracks inside concrete is harmful to the structural durability of seawater coral aggregate concrete (CAC) subjected to an aggressive marine environment. Thus, three-point bending (TPB) tests were performed on the notched beams to determine the fracture properties of cement-based CAC and slag-based alkali-activated CAC (AACAC) at different initial crack-depth ratios (a(0)/H = 0.2, 0.3, 0.4, and 0.5) and alkaline contents (Na2O-to-binder ratios of 3%, 4%, and 6% by mass). The initial fracture toughness (K-IC(ini)), critical effective crack length (a(c)), and unstable fracture toughness (K-IC(ini))( )of the CAC and AACAC were calculated and analyzed based on the double-K fracture criterion. Then, the fracture energy (G(F)) and characteristic length (l(ch)) were introduced to analyze the energy consumption and brittleness of concrete. It was found that increasing the a(0)/H ratio reduced the initial cracking load (P-ini), peak load (P-max), a(c), G(F), and l(ch), but increased the P-ini/P(max )ratio, K-IC(ini), K-IC(un), and K-IC(ini)/K-IC(un) ratio, implying that a higher a(0)/H ratio had a detrimental effect on the crack propagation and increased the brittleness of the AACAC. Additionally, a higher alkaline content, i.e., a greater compressive strength of concrete, upgraded the values of P-ini, P-max, K-IC(ini), K-IC(un), and G(F) due to better mechanical interaction at paste-aggregate interfaces. However, the P-ini/P-max ratio, a(c), and l(ch) were steadily lowered with increasing concrete strength, justified by an increase in brittleness. Moreover, the notched AACAC beams contained higher a(c) (approximately 12.2% increase) and lower K-IC(ini)/K-IC(un)(approximately 4.6% decrease) than those of the notched CAC beams, demonstrating that the existence of alkali-activated materials (AAMs) was beneficial to crack propagation due to improved interfacial transition zone (ITZ) between the paste matrix and aggregates.