Abstract:Abstract— Fully reversed low cycle fatigue tests were carried out on 7 mm diameter cylindrical specimens of a dual phase steel treated to give five different microstructures, namely F—ferrite (+ little carbide particles), CF—continuous ferrite + 8.2% martensite, FM—49.1% ferrite + 50.9% martensite mixed structure, CM—continuous martensite + 22.4% ferrite and M—100% martensite. A finite element program was developed based on Eisenberg's cyclic plasticity theory and the low cycle stress‐strain response of the steels with duplex phase microstructures was calculated from the low cyclic curves of the single ferrite (steel F) and martensite (steel M) phase. The experimental results show that fatigue performance of dual phase steel improves as martensite content is increased up to about 50%, thereafter it obviously deteriorates. During cyclic loading, the calculated plastic strain accumulated in ferrite is higher than that in martensite. Inhomogeneity of the plastic strain accumulation in steel CF is more pronounced than that in steel CM. In steel FM a relatively uniform strain distribution was found. Controlling the size of particle phase can result in an optimum strain distribution. Thus, the plastic deformation capability of the constituent phases can be enhanced leading to fatigue performance improvement. Crack initiation occurs easily at the ferrite/martensite interface with a coarse particle phase size, regardless of phase continuity. In steel CF, a crack initiates at the interface perpendicular to the stress axis and propagates in the ferrite matrix by deflecting around coarse martensite particles or by cutting fine martensite particles. In steel CM, a crack initiates at the interface along the stress axis and propagates in the martensite matrix through ferrite particles.

Change Characteristics of Static Mechanical Property Parameters and Dislocation Structures of 45(#) Medium Carbon Structural Steel During Fatigue Failure Process

Variation In Mechanical Properties, Microstructures And Fracture Behavior Of 304 Stainless Steel During Low-Cycle Fatigue

Effects of low-cycle fatigue on static mechanical properties, microstructures and fracture behavior of 304 stainless steel

Effect of cyclic straining at elevated-temperature on static mechanical properties, microstructures and fracture behavior of nickel-based superalloy GH4145/SQ

A New Approach to Low-Cycle Fatigue Damage Based on Exhaustion of Static Toughness and Dissipation of Cyclic Plastic Strain Energy During Fatigue

A New Approach for Studying Fatigue Damage

Mesoscopic mechanical properties of 18Cr-8Ni austenitic steel subjected to low-cycle fatigue loading

Improved Ultra-Low Cycle Fatigue Fracture Models for Structural Steels Considering the Dependence of Cyclic Damage Degradation Parameters on Stress Triaxiality

Fatigue hardening/softening behaviour investigated through Vickers microhardness measurement during high-cycle fatigue

Investigation of fatigue mechanical properties of apolycrystalline solid at mesoscopic scale using depth-sensing indentation (DSI) technique

Abnormal Relation Between Tensile and Fatigue Strengths for a High-Strength Low-Alloy Steel

Low-cycle Fatigue Testing and Microstructure of High Strength-Ductility Structural Steel Materials

Experimental Investigation on Low-Cycle Fatigue Damages of High Strength-Ductility Steels

Experimental and Numerical Investigation of Ductile Fracture of Carbon Steel Structural Components

Experimental and Constitutive Model Study of Structural Steel under Cyclic Loading

Low Cycle Fatigue Property and Fracture Behavior of Low Yield Point Steels

Study on fatigue temperature evolution and failure behavior of Q460 steel

Extremely - low cycle fatigue fracture of Q235 steel at different stress triaxialities

EXPERIMENTAL INVESTIGATION ON FATIGUE PROPERTIES OF Q345QD AND ITS FATIGUE FRACTURE MECHANISM

LOW‐CYCLE FATIGUE INVESTIGATIONS AND NUMERICAL SIMULATIONS ON DUAL PHASE STEEL WITH DIFFERENT MICROSTRUCTURES

Experimental Study of Structural Steel Constitutive Relationship under Cyclic Loading