A Highly Stable Reinforced PEM Assisted by Resveratrol and Polydopamine-Treated PTFE

Youxiu Huo,Qingbing Li,Zhiyan Rui,Rui Ding,Jia Liu,Jia Li,Jianguo Liu

DOI: https://doi.org/10.1016/j.memsci.2021.119453

IF: 9.5

2021-01-01

Journal of Membrane Science

Abstract:The need to reduce the cost of proton exchange membranes (PEMs) leads to less usage of perfluorinated sulfonic acid (PFSA), which would definitely result in a decline in the membrane lifespan under the attack of free radicals. In this study, polytetrafluoroethylene (PTFE) is used as a reinforced material to make a thinner composite membrane due to the poor mechanical strength of the pristine membrane. Moreover, a polydopamine (PD)treated strategy was selected to make hydrophilic PTFE, which allows the adoption of a high-boiling point solvent for the dissolution of resveratrol, a natural antioxidant produced by plants that acts as a free radical scavenger (FRS) in the membrane to prevent the membrane from being attacked. With the help of dimethyl formamide (DMF), a high-boiling point solvent, and hydrophilic groups in PD molecules, a Nafion/PD@PTFE/ resveratrol composite membrane with a thickness of 10 mu m was prepared and tested using an accelerated degradation test (ADT) strategy. With a resveratrol dose of 1 wt%, the cell presented a lower hydrogen crossover of 2.82 mA cm-2 and a longer lifespan than those of a membrane without resveratrol while cell performance did not suffer too much damage. In the ADT experiment, the hydrogen crossover of Nafion/PD@PTFE/resveratrol was still less than 20 mA cm-2 after 8 open circuit voltage (OCV) cycles, while that without resveratrol increased to 80 mA cm-2 in 3 OCV cycles.