Abstract:Transition-metal nanoparticles (NPs) have been widely used as high performance catalyst in organic reactions, and it is well recognized that these metal species are highly toxic, their handling is hazardous, and featured also by high-costing. Their incorporation in or immobilization on a support is one of the most opted strategies. We report here a facile two-step protocol to obtain composite microspheres () of porous polyurea microspheres (PPM) and Pd-NPs: highly uniform PPM were prepared first by interfacial polymerization of toluene diisocyanate in water through a microfluid device, followed by Pd immobilization on their surface. was characterized by NMR, XPS, and temperature-programmed reduction. The results indicated that Pd was immobilized on PPM surface through a coordination interaction with urea ligand. A parallel version of the composite microspheres, , was also prepared through one single step, by dissolving Pd(OAc)2Pd in the monomer in PPM preparation. The catalytic performance of the two composite microspheres, and , was evaluated in the reduction of 4-nitrophenol (4-NP) and in degradation of several dyes, using NaBH4 as the reducer in both, and the results compared. In all the tested processes, out-performed , thanks to their higher specific surface area of immobilized Pd-NPs and a larger number of active sites on the surface. The catalysts were shown also to have sustainable reusability in dyes degradation. In contrast, the catalytic activity was obviously deteriorated in its reuse in 4-NP reduction, owing to the formation of a complex between Pd-NPs and the reduction product of 4-NP, which resulted in the Pd active sites being covered by the complex, leading to the decrease in their catalytic performance. Their good reusability in dyes degradation confirmed that the decrease in catalytic activity was limited only to the processes where 4-aminophenol and similar amine containing compounds were involved. The high uniformity, easy recovery, high catalytic activity and sustainable reusability make a great catalyst with good potential for applications in different fields.

Catalytic Reduction of Nitrophenol and MB Waste Water Using Homogeneous Pt NPs Confined in Hierarchically Porous Silica

Application of Pd/C Catalyst to Degradation and Utilization of Nitrobenzene in Water

Catalytic Reduction of p-Nitrophenol on MnO2/Zeolite -13X Prepared with Lawsonia inermis Extract as a Stabilizing and Capping Agent

High-Performance Catalytic Reduction of 4-Nitrophenol to 4-Aminophenol over Pt Nanoparticles Supported on Co-Al LDH Nanosheets

High-efficient Catalytic Reduction of 4-Nitrophenol Based on Reusable Ag Nanoparticles/graphene-Loading Loofah Sponge Hybrid.

Catalytic pyrolysis of wood biomass in an auger reactor using calcium-based catalysts.

Rational Fabrication of Ti0.69Zr0.31O2 Modified Au-loaded Halloysite Core-Shell Catalyst for Highly Efficient Reduction of 4-Nitrophenol and Dye Pollutants

Rational fabrication of Ti 0.69 Zr 0.31 O 2 modified Au-loaded halloysite core-shell catalyst for highly efficient reduction of 4-nitrophenol and dye pollutants

Cu2S/Ni3S2 Nanosheets Combined with Nickel Foam Substrate for Efficient Catalytic Ozonation of P-Nitrophenol in Wastewater

Advancing nitrate reduction to ammonia: insights into mechanism, activity control, and catalyst design over Pt nanoparticle-based ZrO2

Pd@Na-CMC/g-C3N4: A nanostructured catalyst system based on sodium carboxymethyl cellulose/graphitic carbon nitride hydrogel beads and its performance in the treatment of organic and inorganic pollutants in water

Porous polyurea microspheres with Pd immobilized on surface and their catalytic activity in 4-nitrophenol reduction and organic dyes degradation

Palladium nanoparticles anchored on NiO particles-modified micro-size chitosan spheres: A promising, active, and retrievable catalyst system for treatment of environmental pollutants

Nanostructures embedded on porous materials for the catalytic reduction of nitrophenols: a concise review

One-Pot Synthesis of Ultra-Small Pt Nanoparticles-Loaded Nitrogen-Doped Mesoporous Carbon Nanotube for Efficient Catalytic Reaction

Efficient catalytic degradation of p-nitrophenol using a novel 2D nanoflake array MWCNTs/PPy/PDA-nZVI catalyst

Promotional effect of embedded Ni NPs in alginate-based carbon toward Pd NPs efficiency for high-concentration p-nitrophenol reduction

Porous chitosan quaternary ammonium salt hydrogel embedded with Cu, Ni and Pd nanoparticles for efficient coupled adsorption-catalytic reduction of methylene blue and 4-nitrophenol

A stable hybrid catalyst (POM-PPPh 3 /L/Ni) for the reduction of toxic nitroarene compounds in water

Strategy to improve gold nanoparticles loading efficiency on defect-free high silica ZSM-5 zeolite for the reduction of nitrophenols

Mesoporous silica nanospheres supported atomically precise palladium nanocluster: Highly efficient and recyclable catalysts in the reduction of 4‐nitrophenol and Heck reactions