Effect of Low-Temperature Tempering on Confined Precipitation and Mechanical Properties of Carburised Steels

Qing Tao,Jian Wang,E. Galindo-Nava
DOI: https://doi.org/10.1016/j.msea.2021.141688
IF: 6.044
2021-01-01
Materials Science and Engineering A
Abstract:Surface-carburised steels are widely used in gears and bearings. The mechanical properties of the surface layers are crucial to improve contact fatigue and anti-wear performance. In this study, the effect of low-temperature tempering on confined precipitation and mechanical properties across surface layers in a high-alloy carburising steel (18Cr2Ni4W) were investigated. The steel was tempered at 240 degrees C with different tempering durations. Microstructure changes, including confined precipitation, and local mechanical properties were analysed layerby-layer. During tempering, the morphology and size of martensite remained unchanged while confined precipitation occurred in martensitic matrix; coherent epsilon phase precipitates formed after 1.5 h, they then transformed to less coherent. phase within 3 h and subsequently evolved to non-coherent. phase after 3 h of tempering. After tempering for 1.5 h, the strength and ductility of the surface layers reach a maximum value, and elongation of the surface layers with high carbon content is comparable to that of the core with low carbon content. It is revealed that the coherent e precipitates are mainly responsible for the increase in strength; whilst ductility of the martensitic matrix increases due to a reduced carbon concentration, avoiding tempering brittleness. The results are valuable to the optimisation of surface properties of carburised steels using lower temperature tempering.
What problem does this paper attempt to address?