Effect of Potassium on the Performance of a CuSO4/TiO2 Catalyst Used in the Selective Catalytic Reduction of NOx by NH3
Yanke Yu,Mengqiao Geng,Desheng Wei,Chi He
DOI: https://doi.org/10.3866/pku.whxb202206034
2023-01-01
Acta Physico-Chimica Sinica
Abstract:Owing to its renewability,abundance,and low environmental impact,biomass is considered to be a viable eco-friendly fuel.Various biofuel-fired power plants have been built worldwide to reduce carbon emissions.Potassium(K)is a typical impurity in the flue gas from biofuel combustion that can deactivate the catalyst used in the selective catalytic reduction of NOx by ammonia(NH3-SCR).CuSO4/TiO2,with excellent sulfur dioxide tolerance,is thought to be a promising vanadium-free catalyst for NH3-SCR;however,the influence of K on the CuSO4/TiO2 catalyst is still unknown.Therefore,in this study,the effect of K on the NH3-SCR performance of CuSO4/TiO2 were investigated and compared with the effect on the performance of the commercial V2O5-WO3/TiO2(VWTi)catalyst.K-poisoned catalysts were prepared via wet impregnation using potassium acetate as the K source.Nitrogen(N2)adsorption-desorption,X-ray diffraction(XRD),X-ray photoelectron spectroscopy(XPS),NH3-temperature programmed desorption(NH3-TPD),H2-temperature programmed reduction(H2-TPR),and in situ diffuse reflectance infrared Fourier-transform spectroscopy(in situ DRIFTS)were used to characterize the prepared catalysts.The NOx conversion over CuSO4/TiO2 with 1.0％(w)K was 92.1％(at 350℃),which was higher than the conversion(75.1％)achieved over the commercial VWTi catalyst with the same K content.The XRD,XPS,and H2-TPR results suggested that K reacted with the CuSO4 in the CuSO4/TiO2 catalyst to form CuO and K2SO4.The presence of CuO enhanced the oxidation of NH3 to N2O,NO,and NO2 during NH3-SCR,thereby decreasing the NOx conversion and N2 selectivity over CuSO4/TiO2.Moreover,based on the results from NH3-TPD and in situ DRIFTS of NH3 adsorption,it can be concluded that the Bransted acid sites(S-OH)were poisoned by K,which restrained the adsorption of NH3 on CuSO4/TiO2.Additionally,the high K content altered the pore structure of the catalyst,leading to a decrease in the specific surface area.However,according to the in situ DRIFTS results,NH3-SCR over K-poisoned CuSO4/TiO2 still followed the Eley-Rideal mechanism:First,NH3 was adsorbed on the Lewis and Br?nsted acid sites of the catalyst,and then gaseous NO and O2 reacted with the adsorbed NH3/NH4 on the acid sites,resulting in the formation of N2 and H2O.Notably,the abundance of acid sites and surface-adsorbed oxygen species on CuSO4/TiO2 could be the main reason for its higher resistance to K-poisoning.In conclusion,our current findings suggested that CuSO4/TiO2 might be a suitable NH3-SCR catalyst for use in the flue gas streams from biofuel-fired power plants.