Abstract:Sulfur oxides present in flue gas can deactivate metal oxide catalysts or metal cation exchange zeolite catalysts used in NH 3 -SCR, as the deposition of (NH 4 ) 2 SO 4 /NH 4 HSO 4 and metal sulfate can obstruct and damage active sites, respectively. The physical poisoning of the (NH 4 ) 2 SO 4 /NH 4 HSO 4 deposition can be prevented by selecting an appropriate reaction temperature range (reversible), while chemical poisoning caused by the sulfation of active sites is challenging to avoid and can permanently deactivate the catalyst (irreversible). This research addresses the issue of irreversible catalyst deactivation resulting from sulfur poisoning by employing metal-free β zeolite without redox sites, which effectively prevents redox site sulfation at its source and shields the catalyst from physical poisoning by operating at moderate to high temperatures. This metal-free β zeolite with an appropriate pore structure exhibited exceptional deNO x activity, N 2 selectivity, stability, and sulfur resistance at 300 °C. The NO oxidation experiment and DFT analysis demonstrated that the specific pore structure of β zeolite functioned as a sub-nano reactor, facilitating the oxidation of NO to NO 2 , thereby triggering the subsequent series catalytic reaction of "fast" SCR. Even in an atmosphere with a high concentration of 300 ppm SO 2 , the β zeolite catalyst maintained over 80 % NO x conversion after 130 h. The slight reduction in activity was attributable to the inhibitory influence of SO 2 on the collision reaction between NO and O 2 ; however, SO 2 did not have any poisonous impact on the catalyst. The unique design strategy found in present work provides valuable insights for the sulfur resistance of metal-free zeolites used in NH 3 -SCR process, and provides a new idea for the design of completely sulfur-resistant catalysts.

Unlocking Mixed-Metal Oxides Active Centers via Acidity Regulation for K&SO 2 Poisoning Resistance: Self-Detoxification Mechanism of Zeolite-Confined de NO x Catalysts

Unraveling Alkali-Tolerance Role of Zeolite Coupling CeWOx Catalyst for NOx Reduction

Discovering the Remarkable Denox Activity and Anti-K Poisoning of MnFeOx/H-Beta Composite Catalyst

Promoting Metal Oxides–zeolite Electron Interaction on MnCeOx/HY Catalyst for Boosting Nitrogen Oxides Reduction

Cu-SSZ-13 zeolite–metal oxide hybrid catalysts with enhanced SO2-tolerance in the NH3-SCR of NOx

Unraveling alkali-tolerance role of zeolite coupling CeWOx catalyst for NO reduction

High-Performance Strategy and Degradation Mechanism of Cezrvox Catalysts for Nox Reduction

NOx Reduction with Resistance Against Multiple Poisoning Agents over Inherent SO42‐ Modified V2O5/CeO2 Catalysts

New Insight into the in Situ SO2 Poisoning Mechanism over Cu-SSZ-13 for the Selective Catalytic Reduction of NOx with NH3

Metal-free β zeolite used as an efficient NH 3 -SCR catalyst can achieve complete immunity to SO 2 : Unique design strategy of sulfur-resistant catalyst

Novel shielding and synergy effects of Mn-Ce oxides confined in mesoporous zeolite for low temperature selective catalytic reduction of NOx with enhanced SO2/H2O tolerance

Mechanistic Investigation of the Enhanced SO2 Resistance of Co-modified MnOx Catalyst for the Selective Catalytic Reduction of NOx by NH3

Alkali poisoning of Fe-Cu-ZSM-5 catalyst for the selective catalytic reduction of NO with NH3

Self-Protected CeO2-SnO2@SO42-/TiO2 Catalysts with Extraordinary Resistance to Alkali and Heavy Metals for NOx Reduction

Support promotion effect on the SO2 and K+ co-poisoning resistance of MnO2/TiO2 for NH3-SCR of NO

Design Strategies for A Denitrification Catalyst with Improved Resistance Against Alkali Poisoning: the Significance of Nanoconfining Spaces and Acid-Base Balance

SO 2 and H 2 O Poisoning Resistance of Manganese Oxide-Based Catalysts for Low-Temperature Selective Catalytic Reduction of NO X

Self-Protection Mechanism of Hexagonal Wo3-Based Deno(X) Catalysts Against Alkali Poisoning

Insight into the Alkali Resistance Mechanism of FeMoTiO x Catalysts for NH 3 Selective Catalytic Reduction of NO: Self-Defense Effects of MoO x for Alkali Capture

Strong metal oxide-zeolite interactions during selective catalytic reduction of nitrogen oxides

Insight into the SO2 poisoning of heterobimetallic FeCu‐SSZ‐13 zeolite in NH3‐SCR reaction