Effect of Grain Boundary Precipitation on Elastic Properties of Cu-2.0%Be Alloy

Zhang Weiwei,Zhao Zhihe,Fang Jihua,He Ping,Chao Zhenlong,Chen Guoqin,Jiang Longtao
2021-01-01
Rare Metal Materials and Engineering
Abstract:The morphology of discontinuous precipitates at the grain boundary of Cu-2.0wt%Be alloy and the relationship between the discontinuous precipitates and heat treatment parameters were studied. The heat treatment parameters were selected by orthogonal experimental design, and the samples with a large difference in microstructure were prepared. The results show that the discontinuous precipitates mainly exist at the grain boundary and are mainly composed of gamma phase and alpha matrix phase. According to the results of range analysis, the main heat treatment parameters affecting grain boundary reaction amount are secondary aging temperature, followed by primary aging time and secondary aging time. The analysis of anelastic behavior shows that the grain boundary reaction amount has a great influence on the deformation of the sample during loading. This is due to the non coherent relationship between the gamma phase formed by discontinuous precipitation and the matrix. There is a disordered region around the gamma phase, where the annihilation of dislocations causes the rearrangement of atoms, resulting in crystal slip and plastic deformation of the alloy. However, the two sides of the grain boundary without boundary reactants are crisscrossed with gamma' phase, where dislocations are easy to pile up and hinder the crystal sliding.
What problem does this paper attempt to address?