Abstract:In this study, thin-wall Mg-6.03Zn-0.55Zr alloy tubes consisted of fine dynamic recrystallized (DRXed) grains and ultrafine grains were successfully obtained by hot spinning process. The results showed that the microstructures of the initial extruded tubes were greatly refined with average grain sizes of 4.46–10.32 µm (300–450 ℃) due to the DRX process, especially at low spinning temperatures. Moreover, the basal texture was transformed from extruded fiber texture to spun tilted plane texture with an angle of ∼10° deviated from the axial direction (AD). More specifically, the basal texture was weakened along AD but was strengthened along the transverse direction (TD) compared with the extruded texture due to the reduced difficulty in pyramidal <c+a> slip activation and the shear deformation induced by the rollers. Consequently, the spun Mg-6.03Zn-0.55Zr alloys showed significant yield asymmetry along AD and TD at room temperature and the increase in spinning temperature had a negative influence on yield strength (YS) that the YS along AD decreased from 290 ± 5 MPa (300 ℃) to 232 ± 2 MPa (450 ℃) and the YS along TD decreased from 236 ± 6 MPa (300 ℃) to 198 ± 4 MPa (450 ℃). Both texture and grain refinement were the important factors in the mechanical properties according to the Hall-Petch relationship due to the varied activation fractions of deformation modes along AD and TD, especially the activation of prismatic <a> slip. Moreover, the fracture mechanism of the spun alloys consisting of fine DRXed grains and ultrafine grains was unusual. The aggregated ultrafine grains played a negative role in the fracture mechanism, because the ultrafine grains were transformed from the dislocation cells and the micro-crack easily occurred in the ultrafine grains.

Microstructure Evolution and Strengthening Mechanisms of Mg-6Gd-4Y-0.5Zn-0.5Zr Alloy During Hot Spinning and Aging Treatment

Microstructure Evolution and Properties of Mg-9Gd-0.8Al Alloy with Lamellar Phase During Extrusion at Different Temperatures

Effects of solid solution and aging process on microstructure and mechanical properties of Mg-Gd-Y alloy

Microstructure and Mechanical Properties of Mg-Xy-1.5mm-0.4zr Alloys

Investigations on Microstructure and Mechanical Properties of Cast Mg-Gd-Y-Zn-Zr-Nd Alloy

Microstructure Evolution and Mechanical Properties of High Performance Mg–10Gd–2Y–0·5Zn–0·3Zr Alloy During Heat Treatments

Microstructure and mechanical properties of Mg-12Gd-5Y-1Sm-0.5Zr alloy

Microstructure characteristics, yield asymmetry and fracture mechanism of the fine grained thin-wall Mg-6.03Zn-0.55Zr tubes fabricated by hot spinning

Microstructure and Strengthening Mechanism of a Thermomechanically Treated Mg–10Gd–3Y–1Sn–0.5Zr Alloy

Microstructure and properties of Mg-9Gd-4Y-1Zn-0.5Zr alloy

Microstructural evolution and enhanced mechanical properties of Mg–Gd–Y–Zn–Zr alloy via centrifugal casting, ring-rolling and aging

Microstructure and Strengthening Mechanism of High Strength Mg–10Gd–2Y–0.5Zr Alloy

Effects of extrusion process on microstructure, precipitates and mechanical properties of Mg-Gd-Y-Zr-Ag alloys

Influence of Heat Treatment on the Evolution of Microstructure and Mechanical Properties of Mg-7Gd-5Y-0.6Zn-0.8Zr Magnesium Alloy

Micro-Shear Bands and Their Enhancement on High Temperature Strength of Mg-Gd-Y-Zr Alloy

Microstructure and Mechanical Properties of Extruded Mg–8.5Gd–2.3Y–1.8Ag–0.4Zr Alloy

Microstructure and Mechanical Properties of Extruded Mg-Zn-Y Alloy

Effects of Heat Treatments on Microstructure and Mechanical Properties of Mg–11Y–5Gd–2Zn–0.5Zr (wt.%) Alloy

Microstructure and Mechanical Properties of Mg–2.0Gd–1.2Y–1.0Zn–0.2Zr Alloy

Microstructure and mechanical properties of Mg-Gd-Zn-Zr alloy after hot extrusion

Microstructure and Mechanical Properties of Mg–Gd–Y–Zn–Zr Alloy Sheets Processed by Combined Processes of Extrusion, Hot Rolling and Ageing