Design of a High-Efficiency and -Gain Antenna Using Novel Low-Loss, Temperature-Stable Li 2 Ti 1 – x (Cu 1/3 Nb 2/3 ) x O 3 Microwave Dielectric Ceramics
Huan-Huan Guo,Mao-Sen Fu,Di Zhou,Chao Du,Peng-Jian Wang,Li-Xia Pang,Wen-Feng Liu,Antonio Sergio Bezerra Sombra,Jin-Zhan Su
DOI: https://doi.org/10.1021/acsami.0c18836
2020-12-24
Abstract:Microwave dielectric ceramics are vital for filters, dielectric resonators, and dielectric antennas in the 5G era. It was found that the (Cu<sub>1/3</sub>Nb<sub>2/3</sub>)<sup>4+</sup> substitution can effectively adjust the TCF (temperature coefficient of resonant frequency) of Li<sub>2</sub>TiO<sub>3</sub> and simultaneously increase its <i>Q</i> × <i>f</i> (<i>Q</i> and <i>f</i> denote the quality factor and the resonant frequency, respectively) value. Notably, excellent microwave dielectric properties (ε<sub>r</sub> (permittivity) ≈ 18.3, <i>Q</i> × <i>f</i> ≈ 77,840 GHz, and TCF ≈ +9.8 ppm/°C) were achieved in the Li<sub>2</sub>Ti<sub>0.8</sub>(Cu<sub>1/3</sub>Nb<sub>2/3</sub>)<sub>0.2</sub>O<sub>3</sub> (LTCN<sub>0.2</sub>) ceramic sintered at 1140 °C. Additionally, the sintering temperature of LTCN<sub>0.2</sub> was reduced to 860 °C by the addition of 3 wt % H<sub>3</sub>BO<sub>3</sub>, exhibiting superior microwave dielectric properties (<i>ε</i><sub>r</sub> ≈ 21.0, <i>Q</i> × <i>f</i> ≈ 51,940 GHz, and TCF ≈ 1.4 ppm/°C) and being chemically compatible with silver. Moreover, LTCN<sub>0.2</sub> + 3 wt % H<sub>3</sub>BO<sub>3</sub> ceramics were designed as a patch antenna and a dielectric resonator antenna, both of which showed high simulated radiation efficiencies (88.4 and 93%) and gains (4.1 and 4.03 dBi) at the center frequencies (2.49 and 10.19 GHz). The LTCN<sub>0.2</sub> + 3 wt % H<sub>3</sub>BO<sub>3</sub> materials have promising future application for either 5G mobile communication devices and/or in low-temperature co-fired ceramic technology owing to their high <i>Q</i>, low sintering temperature, small density, and good temperature stability.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsami.0c18836?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsami.0c18836</a>.Refined lattice parameters of LTCN<i><sub>x</sub></i> (0 ≤ <i>x</i> ≤ 0.4) ceramics (Table S1), Raman spectra of LTCN<i><sub>x</sub></i> (0 ≤ <i>x</i> ≤ 0.4) ceramics (Figure S1), SEM images and densities of the LTCN<sub>x</sub> (0 ≤ <i>x</i> ≤ 0.4) specimens (Figure S2), phonon parameters achieved from the fitting of the infrared reflectivity spectra of the LTCN<sub>0.2</sub> specimen (Table S2), phonon parameters achieved from the fitting of the infrared reflectivity spectra of the LTCN<sub>0.2</sub> + 3 wt % H<sub>3</sub>BO<sub>3</sub> ceramic (Table S3), and optimized parameters of the proposed patch antenna (Table S4) (<a class="ext-link" href="/doi/suppl/10.1021/acsami.0c18836/suppl_file/am0c18836_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,nanoscience & nanotechnology