Temperature-stable Na0.5Bi0.5TiO3-based Relaxor Ceramics with High Permittivity and Large Energy Density under Low Electric Fields

Guoliang Xue,Xuefan Zhou,Zhongna Yan,Gang Liu,Hang Luo,Dou Zhang

DOI: https://doi.org/10.1016/j.jallcom.2021.160755

IF: 6.2

2021-01-01

Journal of Alloys and Compounds

Abstract:Nowadays, it remains a challenge to achieve a simultaneous improvement of dielectric constant, energy density, and temperature stability in dielectric ceramics. In this work, it was found that such drawback could be effectively resolved by using KTaO3 to substitute Na0.5Bi0.5TiO3. In (1-x)Na(0.5)Bi(0.5)TiO(3-)xKTaO(3) ceramics, the temperature coefficient of capacitance (TCC) of x = 0.10 composition is lower than 15% in the temperature range of 25-390 degrees C, with a high dielectric constant of 2008 and a low dielectric loss of 0.0044 at 150 degrees C. Meanwhile, a large discharged energy density of similar to 2.50 J/cm(3) with the variation less than +/- 3% in 5-190 degrees C was obtained under a low electric field of 18 kV/mm in x = 0.20 composition, accompanied with a high energy efficiency of > 80%. These results reveal that this ceramic system is a promising candidate for temperature-stable dielectric and energy storage capacitors applications. (C) 2021 Elsevier B.V. All rights reserved.