Abstract:Despite that multi-modal hierarchically porous metal-organic frameworks (MOFs) are highly desirable due to their capability for the spatial organization of different host reaction, their facile synthesis templated by a single surfactant system is still challenging. Herein, we developed a temperature-controlled strategy to synthesize trimodal hierarchically porous Ce-based UiO-66-type MOFs (THPUiO(Ce)) with tailorable core-shell configurations by using nanoemulsions as soft templates. The hierarchical pore sizes and structures of cores and shells are controllable by facilely manipulating two-step temperatures and the components of the nanoemulsion. For a given nanoemulsion system, when the initial synthetic temperature is higher than the second one, the resultant THPUiO(Ce) is composed of dendritic channels (30-50 nm) in cores and smaller cage-like mesopores (15-20 nm) in shells. Reversely, when the initial synthetic temperature is lower than the second one, the smaller mesopores (around 15 nm) are located in cores surrounded by large pore channels. Similarly, trimodal hierarchically porous bimetallic THPUiO(Ce/Zr) can also be constructed upon extending this temperature-controlled approach, in which the molar ratio of the Zr content could be tuned up to 48%. In virtue of the inhomogeneous nature of THPUiO(Ce), the hollow Ce-based MOFs with mesopores distributed on 60 nm thickness shells can be achieved after the acid treatment of THPUiO(Ce). This facile assembly approach is expected to set a guideline for the construction of hierarchically porous MOFs for potential multicompartmental related applications.

Pre-programed Hydroxy Double Salt Templates for Room-Temperature Controlled Synthesis of Mixed-Metal Zeolitic Imidazolate Frameworks

Deciphering Metal–Organic Framework Synthesis from Hydroxy Double Salts: In-Situ Insights Via Synchrotron X‑ray Diffraction and Absorption Spectroscopy

Facile Conversion of Hydroxy Double Salts to Metal-Organic Frameworks Using Metal Oxide Particles and Atomic Layer Deposition Thin-Film Templates

An Ultrastable Metal–Organic Framework with Open Coordinated Sites Realizing Selective Separation Toward Cationic Dyes in Aqueous Solution

Synthesis of Metal-Organic Frameworks from the System Metal/L-Glutamic Acid/Tea/H2o

Synthesis, Morphology Control, and Properties of Porous Metal–organic Coordination Polymers

Unseeded Organotemplate-Free Hydrothermal Synthesis of Heteroatomic MFI Zeolite Poly-Nanocrystallites

Transformation of Metal-Organic Frameworks for Molecular Sieving Membranes

High-yield synthesis of zeolitic imidazolate frameworks from stoichiometric metal and ligand precursor aqueous solutions at room temperature

Dynamic Bond-Directed Synthesis of Stable Mesoporous Metal-Organic Frameworks under Room Temperature

Controlled synthesis of metal-organic frameworks via AC electrokinetic mixing-assisted microfluidics: A case study of ZIF-8

Template-Free Synthesis Of Hierarchical Porous Metal-Organic Frameworks

One‐Step Room‐Temperature Synthesis of Metal(IV) Carboxylate Metal—Organic Frameworks

Solvent-free mechanochemical route for the construction of ionic liquid and mixed-metal MOF composites for synergistic CO2 fixation

Rapid ultrasound-assisted synthesis of controllable Zn/Co-based zeolitic imidazolate framework nanoparticles for heterogeneous catalysis

Temperature-Controlled Synthesis of Trimodal Hierarchically Porous MOFs with Variable Core–Shell Configurations

Designed assembly of heterometallic zeolite-like framework materials from two different supertetrahedral metal clusters

An efficient modulated synthesis of zirconium metal–organic framework UiO-66

Kinetic-Controlled Formation of Bimetallic Metal-Organic Framework Hybrid Structures.

Mesoporous MFI zeolites with self-stacked morphology templated by cationic polymer.

Effect of Pyrazolium-Derived Compounds As Templates in Zeolite Synthesis