Effect of Pyrazolium-Derived Compounds As Templates in Zeolite Synthesis

Peicheng Wang,Yang Zhao,Hongbin Zhang,Tao Yu,Yahong Zhang,Yi Tang

DOI: https://doi.org/10.1039/c7ra02864d

IF: 4.036

2017-01-01

RSC Advances

Abstract:Novel diquaternary pyrazolium templates with different spatial sizes have unique effects on zeolite phase selectivity and macromorphology.

What problem does this paper attempt to address?

Pre-programed Hydroxy Double Salt Templates for Room-Temperature Controlled Synthesis of Mixed-Metal Zeolitic Imidazolate Frameworks

Yixin Chen,Shuchang Yuan,Yujia Li,Yongqun Ma,Chenxiao Zhang,Ming Zhang,Qiying Mao,Yingwu Luo,Junjie Zhao

DOI: https://doi.org/10.1039/d1ta02814f

IF: 11.9

2021-01-01

Journal of Materials Chemistry A

Abstract:Bimetallic hydroxy double salts pre-programed through co-precipitation were found as excellent templates for mixed-metal MOFs.
Templates for the Synthesis of Zeolites

Huimin Luan,Qinming Wu,Jianping Wu,Xiangju Meng,Feng-Shou Xiao

DOI: https://doi.org/10.1016/j.cjsc.2024.100252

IF: 0.847

2024-01-01

Chinese journal of structural chemistry

Abstract:Though zeolites have been successfully synthesized for several decades,the roles of templates for zeolite synthesis are still not fully understood yet.Currently,many types of templates have been employed such as inorganic alkali metal ions,organic quaternary ammonium cations,organic amines,organic quaternary phosphonium cations,metal complexes and zeolite seeds,and the roles are mainly summarized into three aspects:structure-directing,space-filling and charge-balancing.In order to synthesize zeolites efficiently,the proposed principles to guide zeolite synthesis are the stabilization of energy between templates and zeolite framework,charge density mis-matching(CDM)and structure matching between zeolite frameworks and templates.The purpose of this review is to briefly summarize the progresses in recent years,clearly showing the roles of the templates for zeolite synthesis.
Templates for Synthesis of Zeolites

Huimin Luan,Qinming Wu,Jianping Wu,Xiangju Meng,Feng-Shou Xiao

DOI: https://doi.org/10.1016/j.cjsc.2024.100252

IF: 0.847

2024-02-01

Chinese journal of structural chemistry

Abstract:Zeolites have been successfully synthesized for several decades, the roles of templates for zeolite synthesis were still not fully understood yet. Currently, many types of templates have been employed such as inorganic alkali metal ions, organic quaternaryammonium cations, organic amines, organic quaternaryphosphonium cations, metal complexes, and zeolite seeds, where the roles are mainly summarized into three aspects: structure-directing, space-filling, and charge-balancing. In order to synthesize zeolites efficiently, it is proposed principles to guide zeolites synthesis such as stabilization of energy between templates and zeolites framework, charge density mismatching, structure matching between zeolite frameworks and templates. The purpose of this review is to briefly summarize the progresses in recent years, clearly showing the roles of the templates for zeolite synthesis.

chemistry, inorganic & nuclear,crystallography
Targeted synthesis of zeolites from calculated interaction between zeolite structure and organic template

Qinming Wu,Huimin Luan,Feng-Shou Xiao

DOI: https://doi.org/10.1093/nsr/nwac023

IF: 20.6

2022-02-23

National Science Review

Abstract:Abstract Zeolites, a class of silica-based porous materials, have been widely employed in the of chemical industry such as sorption, separation, catalysis, and ion-exchange. Normally, the synthesis of zeolites is performed in the presence of organic templates from trial-and-error route, which is labor-intensive and empirical. In recent years, theoretical simulation from the interaction between zeolite structure and organic template has been used to guide the synthesis of zeolites, which is time-saving. In this review, the recent progresses for the targeted synthesis of zeolites from interaction between zeolite structure and organic template are briefly outlined including design of new templates for zeolite synthesis, preparation of zeolites with new composition, development of novel routes for zeolite synthesis, synthesis of intergrowth zeolites, generation of novel zeolite structures, control of zeolite morphology, and modulation of aluminum distribution in the zeolites. These targeted syntheses reveal that the minimum energy principle from the theoretical simulation is a key for guiding zeolite crystallization. This review would be important for zeolite researchers to rationally synthesize zeolites and effectively design new zeolite structures.

multidisciplinary sciences
Role of Supramolecular Chemistry During Templating Phenomenon in Zeolite Synthesis

Cecilia Paris,Manuel Moliner

DOI: https://doi.org/10.1007/430_2017_11

2017-01-01

Structure and bonding

Abstract:In the last years, there is an increasing interest in the use of organic molecules with the appropriate functionalities to interact with other organic molecules and/or inorganic cations through non-covalent supramolecular interactions, as very specific organic structure-directing agents (OSDAs) for zeolite synthesis. These assembled molecular subunits allow directing the crystallization of zeolite structures with particular physico-chemical properties, such as novel framework topologies, crystal size, chemical compositions, acid-base properties, or metal incorporation, which otherwise would not be achieved using “classical” amine or ammonium-based OSDA molecules. Along the present chapter, different zeolite synthesis strategies employing assembled molecular subunits will be presented, including the use of crown ether-based supramolecular templates, metal-organic complexes, aromatic molecules able to interact through π–π interactions, or supramolecular assembled amphiphilic molecules, among others. The most relevant results described in the literature using these supramolecular-based templating routes will be discussed, together with the current challenges and perspectives.

chemistry, physical, inorganic & nuclear
Insights into the Organotemplate-Free Synthesis of Zeolite Catalysts

Yeqing Wang,Qinming Wu,Xiangju Meng,Feng-Shou Xiao

DOI: https://doi.org/10.1016/j.eng.2017.03.029

IF: 12.834

2017-01-01

Engineering

Abstract:As the most important nanoporous material, zeolites, which have intricate micropores, are essential heterogeneous catalysts in industrial processes. Zeolites are generally synthesized with organic templates under hydrothermal conditions; however, this method is environmentally unfriendly and costly due to the formation of harmful gases and polluted water. This article briefly summarizes the role of organic templates and describes designed routes for the organotemplate-free synthesis of zeolites, aided by zeolite seeds and zeolite seeds solution. Furthermore, this review explicates that the micropore volume decreases with an increase of the Si/Al ratios in the organotemplate-free synthesis of zeolite products, where Na+ exists as an alkali cation. This feature is very important in directing the synthesis of zeolite catalysts with controllable Si/Al ratios under organotemplate-free conditions, and is thus important for the efficient design of zeolites.
Impact of Synthesis Parameters on the Crystallinity of Macroscopic Zeolite Y Spheres Shaped Using Resin Hard Templates

Zahra Asgar Pour,Edrees Abu Zeitoun,Yasser A. Alassmy,Mustapha El Hariri El Nokab,Paul H. M. Van Steenberge,Khaled O. Sebakhy

DOI: https://doi.org/10.3390/cryst14121051

IF: 2.7

2024-12-03

Crystals

Abstract:In this study, the effects of several synthesis parameters including aging time, micropore-structure-directing agents, and hydrothermal treatment temperature profile were systematically examined with respect to their impact on the crystallinity of macroscopic zeolite Y spheres formed in the presence of organic anion-exchange resin templates. Spherical resins were utilized as hard templates to shape the zeolite Y particles. Zeolite Y precursors were initially deposited into the pores of the resin template and subsequently crystallized over time through precise control over these synthesis parameters. The resulting zeolite Y spheres were characterized using an array of characterization techniques, including XRD, SEM, TEM, BET, FTIR, and XRF. We identify the optimal conditions for maximizing the crystallinity of the macroscopic zeolite Y particles using resin templates as macroscopic shaping agents. This functional material has the potential to be used as both catalyst and adsorbent in several applications.

materials science, multidisciplinary,crystallography
Advances in Synthesis and Application of Extra Large-pore Zeolites Formed by More than 12-member Rings

NIU Guo-xing,SUN Zhe,LI Yan-rong,WANG Ji-feng,YIN Ze-qun,LI Quan-zhi

DOI: https://doi.org/10.15943/j.cnki.fdxb-jns.2009.03.008

2009-01-01

Abstract:Synthesis and application as catalysts of extra large-pore zeolites,which are of silica base and formed by more than 12-member rings are reviewed.The influence of the types of templates,mineralizers and heteroatoms on the structures of zeolites is introduced.Their future development and research trends are also approached.
Seed-directed Synthesis of Zeolites with Enhanced Performance in the Absence of Organic Templates

Bin Xie,Haiyan Zhang,Chengguang Yang,Siyu Liu,Limin Ren,Lin Zhang,Xiangju Meng,Bilge Yilmaz,Ulrich Mueller,Feng-Shou Xiao

DOI: https://doi.org/10.1039/c0cc05414c

IF: 4.9

2011-01-01

Chemical Communications

Abstract:We demonstrate here a seed-directed synthesis (SDS) of Beta, Levyne, and Heulandite zeolites in the absence of organo-templates, where the seeds drive crystallization of the zeolites. Compared with conventional Beta synthesized in the presence of organic templates, Beta-SDS exhibits large textural parameters, stable Al species, and unprecedentedly high density of active sites, resulting in superior catalytic activity and selectivity for valuable products in catalysis.
Influence of various templates on the performance of MFI zeolite in catalytic synthesis of trioxane

Wenhui Wu,Kangrui Zhao,Kun Xiao

DOI: https://doi.org/10.1007/s10934-024-01677-7

2024-08-29

Journal of Porous Materials

Abstract:ZSM-5 is widely used in the field of catalysis due to its stability and tunability. Its acidity can be adjusted not only by varying the initial gel composition, but also by incorporating different types of template to enhance its performance. Both [Ga]-MFI and [Ga, Al]-MFI have demonstrated promising performance in the catalytic trioxane of formaldehyde synthesis. However, there is currently a paucity of research examining the influence of different templates on the catalytic performance of [Ga]-MFI and [Ga, Al]-MFI. The influence of different templates on the structure, morphology, and pore structure of the zeolite has been revealed through the application of characterisation techniques, including XRD, MAS NMR spectroscopy, ICP-OES, BET, and SEM. The impact of different templates on the acid properties of [Ga]-MFI and [Ga, Al]-MFI was assessed using NH 3 -TPD and Py-IR. The results of the experimental investigation into the catalytic performance of zeolites synthesised with larger molecular-structured templates indicate that these zeolites exhibit superior catalytic performance. Furthermore, the introduction of Na + ions has been observed to reduce the space-time yield of the products.

materials science, multidisciplinary,chemistry, physical, applied
Design of an Organic Template for Synthesizing ITR Zeolites under Ge-Free Conditions.

Ye Ma,Junyi Hu,Kai Fan,Wei Chen,Shichao Han,Qinming Wu,Yanhang Ma,Anmin Zheng,Eduard Kunkes,Trees De Baerdemaeker,Andrei-Nicolae Parvulescu,Nils Bottke,Toshiyuki Yokoi,Dirk E. De Vos,Xiangju Meng,Feng-Shou Xiao

DOI: https://doi.org/10.1021/jacs.3c04652

IF: 15

2023-01-01

Journal of the American Chemical Society

Abstract:Germanosilicate zeolites with various structures have been extensively synthesized, but the syntheses of corresponding zeolite structures in the absence of germanium species remain a challenge. One such example is an ITR zeolite structure, which is a twin of the ITH zeolite structure. Through the modification of a classic organic template for synthesizing ITH zeolites and thus designing a new organic template with high compatibility to ITR zeolite assisted by theoretical simulation, we, for the first time, show the Ge-free synthesis of an ITR structure including pure silica, aluminosilicate, and borosilicate ITR zeolites. These materials have high crystallinity, corresponding to an ITR content of more than 95%. In the methanol-to-propylene (MTP) reaction, the obtained aluminosilicate ITR zeolite exhibits excellent propylene selectivity and a long lifetime compared with conventional aluminosilicate ZSM-5 zeolite. The strategy for the design of organic templates might offer a new opportunity for rational syntheses of novel zeolites and, thus, the development of highly efficient zeolite catalysts in the future.
The Effects of Composite Template System with Fluoride on the Acidity of Hβ Zeolite

XL Qi,SJ Li,B Li,N Li,XY Liu,BX Lin

DOI: https://doi.org/10.3321/j.issn:0253-9837.2004.02.019

IF: 16.5

2004-01-01

Chinese Journal of Catalysis

Abstract:The effects of the composite template system with fluoride on the acidity of HP zeolite were investigated systematically by XRD, NH3-TPD, FT-IR and MAS NMR methods and the probe reaction of methanol dehydration. The results showed that the acidity of HP zeolite was related to the synthesis conditions. The composite template system was in favor of the incorporation of Al into the framework of HP zeolite compared with the traditional template system (without fluoride). Furthermore, the total acid sites, especially strong acid sites, in HP zeolite synthesized using the composite template system were more than those in HP zeolite synthesized using the traditional template system owing to the change of aluminum configuration resulted from different crystallization mechanism of HP zeolite. The ratio of strong acid sites to weak acid sites in the former was markedly higher than that in the latter. The catalytic activity of the two HP samples for methanol dehydration was compared, and the results showed that their methanol conversion was 72.6% and 43.5%, respectively, under the conditions of WHSV = 2 h(-1), theta = 180degreesC and t = 8 h.
Highly Selective Synthesis of Large Aromatic Molecules with Nano-Zeolite: Beyond the Shape Selectivity Effect

Yilin Hou,Ning Wang,Jianmei Zhang,Weizhong Qian

DOI: https://doi.org/10.1039/c6ra28844h

IF: 4.036

2017-01-01

RSC Advances

Abstract:We report a combination of the shape selectivity effect of zeolites and external surface alkylation to produce larger molecules.
Mesoporous Y zeolite through ionic liquid based surfactant templating

Alexander Sachse,Caroline Wuttke,Urbano Díaz,Michèle Oberson de Souza

DOI: https://doi.org/10.1016/j.micromeso.2015.05.049

IF: 5.876

2015-11-01

Microporous and Mesoporous Materials

Abstract:New surfactant molecules based on ionic liquids, such as [C16MIm]Cl and [C16MPy]Cl were employed in the rearrangement of Y zeolite to introduce mesopores of different morphologies. We evidence that the templating efficiency of these ionic liquids is identical as for the classically used ammonium based surfactant (CTAC) in the synthesis of siliceous MCM-41. Yet, their templating behavior differs importantly when used in the surfactant templating approach to produce mesoporous Y zeolite. This finding indicates that the micellization ability of these surfactants within the zeolite confined spaces differs to the one in solution and hence has a major impact on the textural properties of the final zeolite phase. Hierarchical porous zeolite Y with novel textural properties could be disclosed.

materials science, multidisciplinary,chemistry, physical,nanoscience & nanotechnology, applied
Unveiling the elusive role of tetraethyl orthosilicate hydrolysis in ionic-liquid-templated zeolite synthesis

X. Li,T.-H. Li,W. Zhou,Y.-P. Li,P.H.-L. Sit,Z. Wu,O.J. Curnow,K.C.-W. Wu,J. Choi,A.C.K. Yip

DOI: https://doi.org/10.1016/j.mtchem.2021.100658

IF: 7.613

2022-03-01

Materials Today Chemistry

Abstract:Despite previous reports showing that crystallization kinetics affects zeolite phase selectivity because zeolites are metastable species in their synthesis solution rather than thermodynamic end points, the critical kinetics-controlling parameter is yet to be determined. This work elucidated the effect of tetraethyl orthosilicate (TEOS) hydrolysis before hydrothermal treatment on the final zeolite phase selectivity in the ionic liquid-templated synthesis of 10-membered ring zeolites (MFI- or TON-type zeolites). The results showed that the dissolved silica concentration in the synthesis solution, which is controlled by varying the TEOS hydrolysis temperature and addition rate, induced heterogeneous nuclear growth. Specifically, in 1-butyl-3-methylimidazolium ([BMIM]Br)-directed syntheses, the high and low concentrations of dissolved silica species led to MFI and TON zeolite formation, respectively. The experimental results are supported by silica polymerization modeling using the Reaction Ensemble Monte Carlo method and theoretical calculations on composite building unit formation. The results are valuable for understanding the nucleation mechanism in zeolite crystallization.

chemistry, multidisciplinary,materials science
The Templating Effect Of An Easily Available Cationic Polymer With Widely Separated Charge Centers On The Synthesis Of A Hierarchical Zsm-5 Zeolite

yicheng zhang,kake zhu,xuezhi duan,xinggui zhou,weikang yuan

DOI: https://doi.org/10.1039/c4ta02325k

IF: 11.9

2014-01-01

Journal of Materials Chemistry A

Abstract:The epichlorohydrin-N, N-dimethyl-1,3-diaminopropane copolymer (PCA) has been introduced for the first time as a meso-template to successfully synthesize a hierarchical ZSM-5 zeolite (PCA-ZSM-5) with mesopores of 7-50 nm in diameter by using small-sized nanoblocks. However, when its structural analogue epichlorohydrin-dimethylamine polyamine (PCS) is used, the obtained ZSM-5 zeolite (PCS-ZSM-5) has lower mesoporosity than ZSM-5 nanocrystallite aggregates (NCA-ZSM-5) synthesized without the meso-template. The templating effect of the two employed cationic polymers (PCS and PCA) on the synthesis of hierarchical ZSM-5 is valuable and interesting to be evaluated, because they are easily available and have common structural characteristics that their macromolecular structure will be largely endangered by the decomposition of quaternary ammonium groups in the long polymer chain. PCA entrapped in the zeolite partially retains its cationic charges and macromolecular structure under hydrothermal conditions and thus has a significant templating effect on the synthesis of hierarchical ZSM-5, which is benefited from the cationic centers widely separated by more than 3 carbons in PCA. However, PCS decomposes severely into small amine molecules, due to the short separation of cationic centers. Further investigation into the templating effect of PCA shows that the small-sized and negatively charged nanoblocks can easily wrap and assemble with PCA and transform into hierarchical ZSM-5 templated by PCA. However, when using large-sized zeolite seeds to synthesize ZSM-5, PCA shows a negligible templating effect because PCA with limited charge density and low accessibility of cationic charges has insufficient interactions with zeolite seeds. The catalytic activities of PCA-ZSM-5 and NCA-ZSM-5 for acetalization of cyclohexanone with methanol are inferior to that of PCS-ZSM-5 with the highest number of acid sites, but the catalytic activities for aldol condensation of benzaldehyde with n-butyl alcohol follow the order of PCA-ZSM-5 > NCA-ZSM-5 > PCS-ZSM-5, consistent with the order of mesoporosity.
Templated Synthesis of Hierarchically Mesoporous Zeolites from Cationic Polymers and Their Excellent Catalytic Properties

Feng-Shou Xiao

2008-01-01

Abstract:Introduction Zeolites with intricate micropores have been widely applied in industry at present, but the relatively small micropores in zeolites significantly influence the mass transport in many catalytic reactions. Recently, mesoporous zeolites from carbon templates have been successfully synthesized [1,2], but their industrial applications are still limited, because of the cost of template, the complexity of synthetic procedures, and the difficulty for dispersion of templates into gels. In this work, at first we describe templated synthesis of a series of hierarchically mesoporous zeolites such as Beta [3] and MFI from the use of mesoscale cationic polymers, then we investigate their catalytic properties in alkylation, cracking, hydrogenation [4], and hydrodesulfurization [5].
Theoretical Design for Zeolite Synthesis

Wu Qinming,Luan Huimin,Xiao Feng-Shou

DOI: https://doi.org/10.1007/s11426-022-1307-5

2022-01-01

Science China Chemistry

Abstract:Zeolites, an important class of microporous crystals, have been widely utilized in the fields of catalysis, ion-exchange, separation, and sorption for a long time. In general, zeolites are synthesized in the presence of costly organic templates under hydrothermal conditions by trial-and-error method, which is not only environmentally unfriendly but also labor-intensive. In recent years, novel concepts of design for zeolite synthesis, which are sustainable, cheap, simple, and efficient, have been developed. In this review, the recent advances in design for zeolite synthesis will be briefly summarized, mainly including the design of organic templates for directing the formation of zeolites, design of organotemplate-free route for zeolite synthesis, design of solvent-free strategy for zeolite synthesis, design for novel interzeolite transformation, and targeted control of zeolite morphologies. This review might be helpful for developing sustainable routes for targeted synthesis of zeolites in the future.
Hierarchial Zeolites: Beyond Creation of Mesoporosity: the Advantages of Polymer‐Based Dual‐Function Templates for Fabricating Hierarchical Zeolites (adv. Funct. Mater. 12/2016)

Qiwei Tian,Zhaohui Liu,Yihan Zhu,Xinglong Dong,Youssef Saih,Jean‐Marie Basset,Miao Sun,Wei Xu,Liangkui Zhu,Daliang Zhang,Jianfeng Huang,Xiangju Meng,Feng‐Shou Xiao,Yu Han

DOI: https://doi.org/10.1002/adfm.201670073

IF: 19

2016-01-01

Advanced Functional Materials

Abstract:A new synthetic strategy is developed for fabricating hierarchically structured zeolite materials, which features the use of cationic non-surfactant polymers as dual-functional templates. Y. Han and co-workers show, on page 1881, that the mutual interpenetration of the polymer and the zeolite networks renders disordered but highly interconnected mesopores in zeolite crystals. This strategy also enables the synthesis of unprecedented core-shell-structured hierarchical zeolites.
Synthesis of Extra-Large Pore, Large Pore and Medium Pore Zeolites Using a Small Imidazolium Cation As the Organic Structure-Directing Agent

Zihao Rei Gao,Salvador R. G. Balestra,Jian Li,Miguel A. Camblor

DOI: https://doi.org/10.1002/chem.202103288

2021-01-01

Chemistry - A European Journal

Abstract:One common strategy in the search for new zeolites is the use of organic structure-directing agents (OSDA). Typically, one seeks to achieve a high specificity in the structure-directing effect of the OSDA. This study shows, however, that an OSDA lacking strong specificity towards any particular zeolite may provide opportunities for discovery when other synthesis parameters are systematically screened. Thus, 1-methyl-2-ethyl-3-n-propylimidazolium has allowed to crystallize the new large/medium pore zeolite HPM-16 as well as the recently reported extra-large pore -SYT and the medium/small pore and chiral STW. The sophisticated OSDA originally affording -SYT and the new simple OSDA have very little in common, both in terms of size, shape and flexibility, while both may still direct the synthesis of the same zeolite. In fact, molecular simulations show that the new OSDA is located in three different positions of the -SYT structure, including the discrete 8MR where the original organic could not fit.

Effect of Pyrazolium-Derived Compounds As Templates in Zeolite Synthesis

Pre-programed Hydroxy Double Salt Templates for Room-Temperature Controlled Synthesis of Mixed-Metal Zeolitic Imidazolate Frameworks

Templates for the Synthesis of Zeolites

Templates for Synthesis of Zeolites

Targeted synthesis of zeolites from calculated interaction between zeolite structure and organic template

Role of Supramolecular Chemistry During Templating Phenomenon in Zeolite Synthesis

Insights into the Organotemplate-Free Synthesis of Zeolite Catalysts

Impact of Synthesis Parameters on the Crystallinity of Macroscopic Zeolite Y Spheres Shaped Using Resin Hard Templates

Advances in Synthesis and Application of Extra Large-pore Zeolites Formed by More than 12-member Rings

Seed-directed Synthesis of Zeolites with Enhanced Performance in the Absence of Organic Templates

Influence of various templates on the performance of MFI zeolite in catalytic synthesis of trioxane

Design of an Organic Template for Synthesizing ITR Zeolites under Ge-Free Conditions.

The Effects of Composite Template System with Fluoride on the Acidity of Hβ Zeolite

Highly Selective Synthesis of Large Aromatic Molecules with Nano-Zeolite: Beyond the Shape Selectivity Effect

Mesoporous Y zeolite through ionic liquid based surfactant templating

Unveiling the elusive role of tetraethyl orthosilicate hydrolysis in ionic-liquid-templated zeolite synthesis

The Templating Effect Of An Easily Available Cationic Polymer With Widely Separated Charge Centers On The Synthesis Of A Hierarchical Zsm-5 Zeolite

Templated Synthesis of Hierarchically Mesoporous Zeolites from Cationic Polymers and Their Excellent Catalytic Properties

Theoretical Design for Zeolite Synthesis

Hierarchial Zeolites: Beyond Creation of Mesoporosity: the Advantages of Polymer‐Based Dual‐Function Templates for Fabricating Hierarchical Zeolites (adv. Funct. Mater. 12/2016)

Synthesis of Extra-Large Pore, Large Pore and Medium Pore Zeolites Using a Small Imidazolium Cation As the Organic Structure-Directing Agent