Microstructures and Mechanical Properties of a Mg–9Gd−3Y−0.6Zn−0.4Zr (wt.%) Alloy Modified by Y-rich Misch Metal

Nan Wang,Qiang Yang,Xinlin Li,Kai Guan,Jingqi Zhang,Caogen Yao,Xuhu Zhang,Jian Meng,Xin Qiu
DOI: https://doi.org/10.1016/j.msea.2020.140609
IF: 6.044
2020-01-01
Materials Science and Engineering A
Abstract:Microstructural evolutions and mechanical properties of a Y-rich misch metal modified Mg-9Gd-3Y-0.6Zn-0.4Zr (wt.%) alloy were investigated. In the as-cast sample, the intermetallic phases are Mg5RE, Mg3RE and 14H-type long-period stacking ordered (LPSO) phase. After solution, all Mg3RE and most Mg5RE were dissolved while the 14H-LPSO plates were coarsened. The as-extruded alloy has a bimodal structure of ultra-fine dynamically recrystallized (DRXed) grains and coarse un-recrystallized grains, and is with a typical non-fiber texture. Disintegrated Mg5RE and 14H-LPSO particles aggregate in extrusion stringers while fine dynamically precipitated Mg5RE particles distribute at grain boundaries. After peak-aging, ultra-thin basal gamma '' and prismatic beta' precipitated in DRXed grain and un-recrystallized regions, respectively. The yield strength of the as-extruded and peak-aged alloys reaches to 385 MPa and 481 MPa, respectively, at room temperature, and to 320 MPa and 350 MPa, respectively, at 250 degrees C. Grain boundary strengthening from both grain boundaries and sub-grain boundaries in DRXed and un-recrystallized regions, respectively, and precipitation strengthening were revealed as the dominant strengthening mechanisms.
What problem does this paper attempt to address?