Synthesis And Characterization Of A New High Temperature Shape Memory Polyimide

Xinli Xiao,Xueying Qiu,Deyan Kong,Wenbo Zhang,Shen Zhang,Yang Hu,Yanju Liu,Jinsong Leng

2015-01-01

Abstract:High temperature shape memory polymers (SMPs) have wide potential applications in various fields, and glass transition temperature (T-g) is a crucial factors in determining their potential applications. Here we report a kind of new shape memory polyimide with a high glass transition temperature (T-g) of 316 degrees C. The polyimide possesses thermal stable but flexible linkages within the backbone, and the number average molecular weight is 61.5 kg mol(-1). The tensile storage modulus of the polyimide decreases slowly with the increase of temperature at glass state, and a sharp glass-rubber transition is observed with a plateau at rubbery state. The storage modulus at 50 degrees C, 260 degrees C and 340 degrees C are 2.3 GPa, 1.3 GPa and 10.1 MPa, respectively. The polymer possesses high thermal stability with the decomposition temperature of 519 degrees C, and the pyrolysis left 56 % carbonaceous char from the aromatic group at 700 degrees C. The sample shows nice shape memory properties with a strain recovery rate of 96.1 % and a strain fixing rate of 97.2 %. The mechanism of high temperature shape memory effect of polyimide is proposed, which will stimulate further research on high temperature SMPs.