Abstract:Low-cycle fatigue (LCF) behavior of nickel-based precipitation-strengthened superalloy GH4145/SQ was investigated systematically under fully reversed total strain amplitude control conditions at 538°C in laboratory air. It was shown that the alloy exhibited a pronounced initial fatigue hardening followed by continuous fatigue softening to failure at high strain amplitudes, while at low strain amplitudes the initial hardening was followed by a well-defined saturation stage. Microstructure observations using optical and transmission-electron microscopy revealed that slip band density increased with increasing total strain amplitudes and the size of the γ′precipitates tended to reduction due to repeated shearing by the dislocations with continuous cyclic straining. The above changes in microstructures during cycling were essentially responsible for the fatigue hardening–softening behavior of the alloy. Both optical and SEM micrographs indicated that at low strain amplitudes crack propagation was basically transgranular, while at high strain amplitudes crack propagation was essentially intergranular. Bilinear behavior with a change of slope at a plastic strain amplitude of about 0.2pct was observed in cyclic stress–strain (CSS), Coffin–Manson (C–M) and plastic strain energy–life plots. A change in the number of operating slip systems and the fracture modes with the strain amplitude employed was used to explain this two-slope characteristic. In both the companion specimens test (CST) and the incremental step test (IST) methods the alloy exhibited non-masing type behavior. It was suggested that, for the first approximation, the half-life plastic strain energy could be calculated directly according to the equation without reckoning in the non-masing behavior.

Damage Behavior of Nb3Sn/Cu Superconducting Strand at Room Temperature under Asymmetric Strain Cycling

Improved Ultra-Low Cycle Fatigue Fracture Models for Structural Steels Considering the Dependence of Cyclic Damage Degradation Parameters on Stress Triaxiality

Low cycle fatigue behavior of nickel-based superalloy GH4145/SQ at elevated temperature

Effect of cyclic straining at elevated-temperature on static mechanical properties, microstructures and fracture behavior of nickel-based superalloy GH4145/SQ

Initial damage influence of stiffness reduction for bronze route Nb3Sn strands

Influence of Strain Amplitude on Low-Cycle Fatigue Behaviors of a Fourth-Generation Ni-Based Single-Crystal Superalloy at 980 °C

Residual Stress in Nb3Sn Superconductor Strand Introduced by Structure and Stoichiometric Distribution after Heat Treatment

Numerical Simulation of the Mechanical Properties of the $\hbox{nb}_{3}\hbox{sn}$ CICCs under Transverse Cyclic Loads

Micromechanical modelling on the elastoplastic damage and irreversible critical current degradation of the twisted multi-filamentary Nb3Sn superconducting strand

Meso-scale low-cycle fatigue damage of polycrystalline nickel-based alloy by crystal plasticity finite element method

Molecular dynamics study of fatigue mechanical properties and microstructural evolution of Ni-based single crystal superalloys under cyclic loading

A modified damage-coupled viscoplastic constitutive model for capturing the asymmetric behavior of a nickel-based superalloy under wide creep-fatigue loadings

Crystal plasticity theory coupled with meso-damage to predict the ratchetting behavior of nickel-based single crystal superalloy

The Effect of Strain and Filament Fracture on the Transport Properties of ITER Cable-in-conduit Conductors

Revealing the influential mechanism of strain ranges on cyclic-life saturation during creep-fatigue in Nickel-based superalloy DZ445

Low Cycle Fatigue Life Evaluation of Notched Specimens Considering Strain Gradient

Cyclic-loading microstructure-property relations from a mesoscale perspective: An example of single crystal Nickel-based superalloys

Structural modeling and mechanical research of carbon nanotube reinforced aluminum matrix composites using strain gradient theory

Strain dependence of critical current and self-field AC loss in Bi-2223/Ag multi-filamentary HTS tapes: a general predictive model

Parametric Study of Cyclic Plasticity Behavior in a Directionally Solidified Superalloy with Partial Recrystallization by Crystal Plasticity Finite Element Simulation

A Simple Phenomenological Model for Characterizing the Coupled Effect of Strain States and Temperature on the Normal-State Electrical Resistivity in Nb3Sn Superconductors