Co-Cu-Al Hydrotalcit: Preparation and Catalytic Activities in No Plus Co Reaction

Hj Li,Xy Jiang,Sl Chen,Xm Zheng

2006-01-01

Chinese journal of inorganic chemistry

Abstract:The catalytic activities of Co-Al hydrotalcite and the addition of transition metal oxides in NO+CO reaction were examined with a microreactor-gas chromatography (GC) reaction system. Experimental results show that Co-Al with addition of Cu cation is with higher catalytic activity for NO + CO reaction, and the activity of Co-Cu-Al hydrotalcite is affected by the molar ratio of Co:Cu:Al. When n(Co):n(Cu):n(Al) was equal to 5:3:1, the activity was the highest with 100% NO conversion at reaction temperature of 120 degrees C. There were two CuO diffraction peaks at 2 theta 35.5 degrees and 38.7 degrees but not a spinel diffraction peaks after Co-Cu-Al (5:3:1) was calcined at 350 Cc. But a small amount of spinel was formed after Co-Cu-Al being calcined at 450 degrees C and the amount of spinel increased with calcination temperature, indicating that spinel formation affected NO reduction. As shown in NO-TPD-MS analysis, the thermal desorption products of NO absorbed on Co-Cu-Al are NO (m/e=30), N2O (m/e=44), N-2 (m/ e=28) and O-2 (m / e=32). We suggest that the desorption species of NO occur at the weak positions of Co-Cu-Al in low temperature but at strong positions in high temperature. In addition, the desorption peak temperature of NO on Co-Cu-Al calcined at 400 degrees C is slightly lower than that calcined at 600 degrees C, indicating that the dissociation of NO oil the surface of Co-Cu-Al is a rate-determining step in NO + CO reaction.