Co-Cu-Al hydrotalcit: Preparation and catalytic activities in NO + CO reaction

LI Hui-Juan,JIANG Xiao-Yuan,CHEN Shun-Lin,ZHENG Xiao-Ming

2006-01-01

Chinese journal of inorganic chemistry

Abstract:The catalytic activities of Co-Al hydrotalcite and the addition of transition metal oxides in NO+CO reaction were examined with a microreactor-gas chromatography (GC) reaction system. Experimental results show that Co-Al with addition of Cu cation is with higher catalytic activity for NO + CO reaction, and the activity of Co-Cu-Al hydrotalcite is affected by the molar ratio of Co∶Cu∶Al. When nCo∶nCu∶nAl was equal to 5∶3∶1, the activity was the highest with 100% NO conversion at reaction temperature of 120 ℃. There were two CuO diffraction peaks at 2θ 35.5° and 38.7° but not a spinel diffraction peaks after Co-Cu-Al (5∶3∶1) was calcined at 350 ℃. But a small amount of spinel was formed after Co-Cu-Al being calcined at 450 ℃ and the amount of spinel increased with calcination temperature, indicating that spinel formation affected NO reduction. As shown in NO-TPD-MS analysis, the thermal desorption products of NO absorbed on Co-Cu-Al are NO (m / e=30), N2O (m / e=44), N2 (m / e=28) and O2 (m / e=32). We suggest that the desorption species of NO occur at the weak positions of Co-Cu-Al in low temperature but at strong positions in high temperature. In addition, the desorption peak temperature of NO on Co-Cu-Al calcined at 400 ℃ is slightly lower than that calcined at 600 ℃, indicating that the dissociation of NO on the surface of Co-Cu-Al is a rate-determining step in NO + CO reaction.