Abstract:Potassium (K) promoter and its loading contents were shown to have remarkable effects on the Fe–O–Si interaction of precipitated Fe/Cu/K/SiO2 catalysts for low-temperature Fischer-Tropsch synthesis (FTS). With the increase in K content from 2.3% (100 g Fe based) up to 7% in the calcined precursors, Fe–O–Si interaction was weakened, as reflected by ATR/FTIR, H2-TPR and XPS investigations. XRD results confirmed that the diffraction peak intensity from (510) facet of χ-Fe5C2 phase strengthened with increasing K loading, which indicates the crystallite size of χ-Fe5C2 increased with the increase in K contents either during the syngas reduction/carburization procedure or after FTS reaction. H2-TPH results indicated that more reactive surface carbon (alpha-carbon) was obtained over the higher K samples pre-carburized by syngas. Raman spectra illustrated that a greater proportion of graphitic carbon was accumulated over the surface of spent samples with higher K loading. At the same time, ATR-FTIR, XRD and Mössbauer spectra (MES) characterization results showed that a relatively higher level of bulk phase Fayalite (Fe2SiO4) species was observed discernibly in the lowest K loading sample (2.3 K%) in this work. The catalytic evaluation results showed that the CO conversion, CO2 selectivity and O/P (C2–C4) ratio increased progressively with the increasing K loading, whereas a monotonic decline in both CO conversion and O/P (C2–C4) ratio was observed on the highest K loading sample during c.a. 280 h of TOS.

Exploration On The Basic Active Centres Of Kf/Al2o3: Effect Of Pretreatment Temperature

Investigation on the solid strong bases derived from supported KF

Basic Properties Of A Kf Modified Alpo4-5 Molecular Sieve

New Solid Base Derived From Alpo4-5 Supported Kf

Investigation on basicity of K2CO3/Al2O3 and KNO3/Al2O3 with probe butene isomerization reaction combined with IR and CO2-STD methods

Promotion Effect Of Kf On The Basic Properties Of Zro2

Temperature-Induced Deactivation Mechanism of Znfe2o4 for Oxidative Dehydrogenation of 1-Butene

Preparation, Characterization and Catalytic Activity Studies of CeO2–K Diesel Soot Oxidation Catalysts Loaded on Porous Al2O3 Substrate Using Water-Immiscible Solvent

Basic Function Of Partially Hydrated Fluoride Species On Supported Kf

Influence of K2NbF7 Catalyst on the Desorption Behavior of LiAlH4

High Field 27al MAS NMR and TPD Studies of Active Sites in Ethanol Dehydration Using Thermally Treated Transitional Aluminas As Catalysts

The effect of potassium on the balance of metal-acid sites in Pt/Al2O3 catalysts and its n-hexane dehydrogenation performance

Reactivity and reaction mechanism of Al-PTFE mechanically activated energetic composites

Attempts to create new shape-selective solid strong base catalysts

Effect of pretreatment conditions on the activity of catalytic reduction of NO over Pt/Al2O3 catalyst

Effect of Alkalis (li, Na, and K) on Precipitated Iron-Based Catalysts for High-Temperature Fischer-Tropsch Synthesis

Activation Temperature Study of Precipitated Fe/Sio2 Catalyst for Fischer-Tropsch Synthesis

A DFT Insight into the Tuning Effect of Potassium Promoter on the Formation of Carbon Atoms via Carburization Gases Dissociation on Iron-Based Catalysts

Effects of Potassium Loading over Iron–Silica Interaction, Phase Evolution and Catalytic Behavior of Precipitated Iron-Based Catalysts for Fischer-Tropsch Synthesis

Influence of CO pretreatment on the activities of CuO/γ-Al2O3 catalysts in CO + O2 reaction

Dehydroaromatization of Methane over Mo/Hzsm-5 Pretreated with Nh4f: Further Study on Effect of Pretreatment Temperature