One-pot Synthesis of Potassium-Functionalized Mesoporous Gamma-Alumina: a Solid Superbase.
Lin Bing Sun,Jing Yang,Jia Hui Kou,Fang Na Gu,Yuan Chun,Ying Wang,Jian Hua Zhu,Zhi Gang Zou
DOI: https://doi.org/10.1002/anie.200800034
2008-01-01
Angewandte Chemie International Edition
Abstract:The synthesis of mesoporous superbases is a challenge for chemists owing to their wide range of potential applications in green chemistry and the difficulties inherent in their preparation. Mesoporous superbasic materials are extremely desirable for use in environmentally benign and economical chemical processes as they can catalyze diverse reactions under mild conditions, therefore many attempts have been made to prepare mesoporous solid bases, for example, by incorporating nitrogen-containing species into mesoporous silica and by grafting organic bases onto mesoporous silica. Owing to the reaction of these strongly basic species with silica, however, most of the solid bases reported to date are relatively weak, which suggests that it is difficult to generate superbasicity on mesoporous silica. In contrast to silica, alumina, especially that of the g-type, is a well-known support for a variety of solid strong bases, which means that the occurrence of mesoporous aluminas affords a good opportunity to prepare mesoporous superbasic materials. Unfortunately, the stability of mesoporous aluminas is relatively poor and structural damage occurs to a greater or lesser extent even if postsynthesis modification is performed carefully. This drawback hinders the application of mesoporous aluminas in preparing solid superbases and other functional materials. Herein we report a new strategy for the one-pot synthesis of potassium-functionalized mesoporous g-alumina that involves the use of K2CO3 to adjust the pH value of the reaction system such that the base precursor KNO3 is produced in situ by hydrolysis of Al(NO3)3. KNO3 is decomposed to the strongly basic species K2O on the g-Al2O3 that is also formed in situ during the same calcination process. This strategy allows the synthesis and modification of mesoporous alumina in a one-pot process, avoids post-treatment framework damage, and saves time and energy. The basic materials obtained exhibit a well-defined mesoporous structure and superbasicity and are active in 1-hexene isomerization, which means that they are valuable candidates for selective adsorption and catalysis involving strong solid bases. The synthetic process is shown schematically in Figure S1 in the Supporting Information. KNO3-coated mesoporous boehmite (AlOOH) with a K/Al atomic ratio (n) of between 0 and 0.27 (Table 1) is obtained initially (denoted as MA-B (n=