Influence Of Span Ratio On The Four-Point Bend End Notched Flexure Test

Biao Li,Yazhi Li

2015-01-01

Abstract:Delamination is one of the primary failure modes for laminated composite structures. Extensive investigations have been made on experimental characterization of interlaminar fracture toughness. Standard test methods are currently available for mode I and mixed mode I+II delamination, and three-point bend End Notched Flexure (3ENF) has recently been standardized as ASTM D7905. However, the interlaminar crack propagation in 3ENF test is conditionally stable and yields only the initiation value of mode II interlaminar fracture toughness, which prevent the measurement of mode II R-curve. Four-point bend End Notched Flexure (4ENF) is another choice in determination of mode II fracture toughness since crack propagation is more stable under displacement controlled load than that of 3ENF. In the present work, the influence of inner to outer span ratio of 4ENF test specimen is experimentally investigated. Span ratios of 40%, 50% and 60% are obtained by varying the inner span while keeping outer span constant. 3ENF test is performed on the same batch of material for comparison. Compliance calibration approach is utilized to establish relationship between crack length and compliance of the specimen, which is further used to evaluate the fracture toughness G(IIC) during fracture tests. The effects of crack initiation from both the Teflon insert end and natural crack front are discussed and compared. It is found that more conservative results are given from natural crack in all test configurations. Experiment results show that span ratio has little influence on the toughness values in the 4ENF tests. The toughness obtained by 3ENF test is 13% to 19% lower than those of 4ENF.