Abstract:DSC, SEM–EDS, XRD and high-temperature XRD analysis was used to study thermal and crystallization behaviour of yttrium aluminate glasses prepared in the form of microspheres. The glasses YA-E (eutectic composition from the pseudo-binary system Al2O3–Y3Al5O12) and YA-G (a composition identical to the stoichiometric Y3Al5O12 (YAG) phase) were prepared by combination of the Pechini method with flame synthesis. The resulting microspheres were largely amorphous, but contained traces of yttrium–aluminium garnet as the main crystalline phase embedded in the yttrium aluminate glass matrix. Crystallization of the YAG phase was observed as the dominant exothermic process on DSC curves. From the DSC records, the basic thermal characteristics of the matrix glass, i.e. Tg (glass transition temperature), Tx (onset of crystallization peak temperature), Tf (temperature of the inflection point of the crystallization peak) and Tp (maximum of crystallization peak temperature), were determined. HT XRD experiments in the temperature interval 750–1200 °C and isothermal HT XRD experiments at 932, 998 and 1200 °C with 6-h holding time were also performed. Crystallization experiments at lower temperatures 932 °C (YA-E) and 915 °C (YA-G) were conducted to study phase development in a low-temperature region. Crystallization experiments at higher temperatures (1000, 1300 and 1500 °C) with maximum holding time of 6 h were performed to study crystallization of α-Al2O3 in the eutectic system. The SEM and SEM–EDS examination of polished cross sections of crystallized microspheres revealed slow volume crystallization of the YAG phase in the AY-E glass. Eventually, polycrystalline microspheres with fine-grained microstructure were prepared after 6-h treatment at 1500 °C.

Phase Selection of YAG Melt under Containerless Solidification Condition

Crystallization kinetics of Al2O3-26mol%Y2O3 glass and full crystallized transparent Y3Al5O12-based nanoceramic

Melt-Casting of Y3al5o12 (yag) Ceramics by Combustion Synthesis under High Gravity with the Addition of Glass

Phase Composition and Structure of Grain Boundary of Oversintered Y3al5o12 Ceramics

Synthesis and crystallization kinetics of Y2CaAl4SiO12 garnet-type glass-ceramic

Synthesis of Nd3+ Doped Nano-Crystalline Yttrium Aluminum Garnet (YAG) Powders Leading to Transparent Ceramic

A Low Viscosity Slurry System for Fabricating Chromium Doped Yttrium Aluminum Garnet (cr:Yag) Transparent Ceramics

Preparation of Infrared Transparent Yag-Based Glass-Ceramics with Nano-Sized Crystallites

Preparation of Yag Glass-Ceramic by Combustion Synthesis under High Gravity

Non‐isothermal crystallization kinetics of Al2O3‐YAG amorphous ceramic coating deposited via plasma spraying

FABRICATION OF TRANSPARENT YAG CERAMICS BY SOLID-STATE METHOD

Pressureless glass crystallization of transparent yttrium aluminum garnet-based nanoceramics

Sintering Behavior, Microstructure and Mechanical Properties of Various Fluorine-Containing Y-SiAlON Glass-Ceramics

Study of thermal behavior and crystallization kinetics of glass microspheres in the Y3Al5O12-Al2O3 system

Thermal behaviour of yttrium aluminate glasses studied by DSC, high-temperature X-ray diffraction, SEM and SEM–EDS

Crystallization Behavior and IR Structure of Yttrium Aluminosilicate Glasses

Phase composition, microstructure, and microwave dielectric properties of non-stoichiometric yttrium aluminum garnet ceramics

Preparation of Transparent YAG Ceramics via a Modified Solid-State Reaction Method

Fabrication of transparent YAG ceramics by traditional solid-state-reaction method

Crystallization and Fluorescence Properties of Ce:Yag Glass-Ceramics with Low Sio2 Content

A novel gelcasting induction method for YAG transparent ceramic