Abstract:DSC, SEM–EDS, XRD and high-temperature XRD analysis was used to study thermal and crystallization behaviour of yttrium aluminate glasses prepared in the form of microspheres. The glasses YA-E (eutectic composition from the pseudo-binary system Al2O3–Y3Al5O12) and YA-G (a composition identical to the stoichiometric Y3Al5O12 (YAG) phase) were prepared by combination of the Pechini method with flame synthesis. The resulting microspheres were largely amorphous, but contained traces of yttrium–aluminium garnet as the main crystalline phase embedded in the yttrium aluminate glass matrix. Crystallization of the YAG phase was observed as the dominant exothermic process on DSC curves. From the DSC records, the basic thermal characteristics of the matrix glass, i.e. Tg (glass transition temperature), Tx (onset of crystallization peak temperature), Tf (temperature of the inflection point of the crystallization peak) and Tp (maximum of crystallization peak temperature), were determined. HT XRD experiments in the temperature interval 750–1200 °C and isothermal HT XRD experiments at 932, 998 and 1200 °C with 6-h holding time were also performed. Crystallization experiments at lower temperatures 932 °C (YA-E) and 915 °C (YA-G) were conducted to study phase development in a low-temperature region. Crystallization experiments at higher temperatures (1000, 1300 and 1500 °C) with maximum holding time of 6 h were performed to study crystallization of α-Al2O3 in the eutectic system. The SEM and SEM–EDS examination of polished cross sections of crystallized microspheres revealed slow volume crystallization of the YAG phase in the AY-E glass. Eventually, polycrystalline microspheres with fine-grained microstructure were prepared after 6-h treatment at 1500 °C.

Crystallization Behavior and IR Structure of Yttrium Aluminosilicate Glasses

Controllable Competitive Nanocrystallization of La3+-based Fluorides in Aluminosilicate Glasses and Optical Spectroscopy

Sintering Behavior, Microstructure and Mechanical Properties of Various Fluorine-Containing Y-SiAlON Glass-Ceramics

Crystallization of LAS glass-ceramics

Synthesis and crystallization kinetics of Y2CaAl4SiO12 garnet-type glass-ceramic

Microstructure and Luminescence of Yb3+-doped Fluorosilicate Glass Ceramics

Dependence of glass -forming ability on starting co mpositions in Y 2O3-Al2O3-SiO2 system

Crystallization kinetics of Al2O3-26mol%Y2O3 glass and full crystallized transparent Y3Al5O12-based nanoceramic

Crystallization kinetics, structural and mechanical properties of transparent lithium aluminosilicate glass-ceramics

Investigation on Crystallization Behavior of Y2O3-Al2O3-SiO2 Glass Prepared by High-gravity Combustion Synthesis

Preparation of Infrared Transparent Yag-Based Glass-Ceramics with Nano-Sized Crystallites

Thermal behaviour of yttrium aluminate glasses studied by DSC, high-temperature X-ray diffraction, SEM and SEM–EDS

Zn–Sr Mixing in the Y-sialon Glass: Formation, Properties and Ballistic Resistance

Effect of P2O5 on Nucleation, Crystallization and Mechanical Properties of Y2O3–Al2O3–SiO2 Glasses

Kinetic analysis of the crystallization of Y2O3 and La2O3 doped Li2O-Al2O3-SiO2 glass

Crystallization and dielectric properties of oxyfluoride aluminosilicate glasses added with Na2O

Structure, Glass Stability And Rheological Properties Of Na2o-Cao-Al2o3-Sio2 Glasses Doped With Y2o3

Effect of Y2O3 Concentration on the Surface and Bulk Crystallization of Multicomponent Silicate Glasses

Effect of P 2 O 5 on Nucleation, Crystallization and Mechanical Properties of Y 2 O 3-Al 2 O 3-Sio 2 Glasses

Crystallization of A High-Strength Lithium Disilicate Glass-Ceramic: an Xrd and Solid-State Nmr Investigation

Deciphering the Glass-Forming Ability of Al2O3-Y2O3 System from Temperature Susceptibility of Melt Structure