Preparation of Infrared Transparent Yag-Based Glass-Ceramics with Nano-Sized Crystallites

Li-Li Wang,Lin Mei,Gang He,Guang-Hua Liu,Jiang-Tao Li,Li-Hua Xu,Zhi-Jun Jiang
DOI: https://doi.org/10.1016/j.jeurceramsoc.2012.03.023
IF: 5.7
2012-01-01
Journal of the European Ceramic Society
Abstract:Transparent YAG-based glass-ceramics were prepared by a novel method called amorphous sintering followed by controlled crystallization (ASCC) from the compositions of 62.5Al2O3–(37.5−x)Y2O3–xLa2O3 (in molar ratio, x=5, 7, 10 and 20). The stability of the YAG glass was improved by the incorporation of La2O3, which increased the activation energy for crystallization. With 10mol% La2O3, bulk YAG glass was prepared by hot-pressing and showed an infrared transmittance of 66%. The YAG glass was converted into glass-ceramics by post annealing at 875°C for 5h for controlled crystallization. The obtained glass-ceramic sample showed a crystallite size of 20–50nm and an infrared transmittance of 60%. With increasing annealing time, the crystallites grew up quickly, resulting in a significant decrease in transparency. In the hot-pressed glass, nano-sized YAG nuclei (∼5nm) were found, which were probably responsible for the crystallization behavior observed at temperatures (e.g. 875°C) below the onset crystallization temperature.
What problem does this paper attempt to address?