Preparation of Β-Mno_2 and Α-Mn_2o_3 Nanorods Via a Self-sacrificing Template Route and Their Characterization and Application
Zhao Hongyuan,Liu Xingquan,Zhang Zheng,Wu Yue,Yang Guang,Chen Bing,Xiong Weiqiang
DOI: https://doi.org/10.7503/cjcu20140670
2015-01-01
Abstract:Pure-phased γ-Mn OOH nanorods were synthesized at 150 ℃ for 20 h through a hydrothermal reaction process,during which KMn O4 was reduced by CH3CH2 OH under autogeneror pressure. With γ-Mn OOH nanorods as self-sacrificing template,β-Mn O2 and α-Mn2O3 nanorods were prepared by calcining at 350 and600 ℃ for 90 min,respectively. The materials were characterized by X-ray diffraction( XRD),scanning electron microscopy( SEM) and thermal-gravimetric analysis( TGA). The results showed that γ-Mn OOH nanorods had good crystallographic quality and the diameters were about 100—300 nm,the length could be as long as several micrometers. The morphology and microstructure were well reserved in β-Mn O2 and α-Mn2O3 products and no other morphology of impurities was observed. With β-Mn O2 and α-Mn2O3 nanorods as manganese sources,spinel Li Mn2O4 samples were prepared by solid state method. At the charge / discharge rate of 0. 5 C,the Li Mn2O4 samples could deliver the initial discharge capacities of 120. 4 and 123. 9 m A·h / g,respectively,and present good cycling stability and rate performance.