Abstract:Hyperbranched polyethylene (HBPE) is a new type of polyethylene materials in addition to low-density polyethylene (LDPE), high-density polyethylene (HDPE), and linear low-density polyethylene (LLDPE). It has dendrimer-like compact globular structures. Due to lack of chain entanglements, it exhibits better solubility and lower viscosity than the other types of polyethylene. HBPE has attracted great attention in the recent years in both academic and industrial researches. However, as polyolefin materials, HBPE suffers from such shortcomings as nonpolar nature and thus lack of functionalities. These shortcomings limit its applications. Grafting of polar molecules such as maleic anhydride (MAH) has been widely adopted in the modification of polyolefins.In this work, HBPE samples having high molecular weight (M-w = 8 x 10(6) g/mol) and high branching density (the number of branches per 1000C = 108) were synthesized by solution polymerization of ethylene with a late transition metal catalyst, namely bi (2, 6-diispropylphenyl) butane diimine nickel dibromide (IBNB) at 45 degrees C and 0.5 MPa. The Ni catalyst is well-known to experience a chain walking mechanism that is responsible for the hyperbranched chain topology. H-1-NMR and C-13-NMR were used to examine the branching density and the type of branches, respectively. It was discovered that the types of branches were mainly methyl (50.54 %) and butyl (20.30%).MAH was grafted onto HBPE through a free radical mechanism. Di-tert amyl peroxide (DTAP) was used as the free radical initiator. However, it was found that the HBPE/MAH/DTAP grafting system experienced severe chain degradation and crosslinking side reactions during the grafting process. N, N-diethyl cinnamamide (DECA) was thus synthesized by the use of cinnamoyl chloride, diethylamine, and triethylamine which was used as an acid-binding reagent. DECA was then used as an inhibitor to suppress the side reactions. The approach was successful and efficient. The gel content in the grafting products was remarkably reduced from 55.38% to 5.15%. The M. was almost doubled in reference to the use of MAH and peroxide DTAP only. The observation suggests that the chain degradation and crosslinking side reactions were dramatically suppressed with the addition of DECA.Compared to the other investigated inhibitors such as styrene (St), N, N-dimethylacetamide (DMAC), 3-(2-furyl) acrylic acid (FAA) and ethyl cinnamate (ECA), DECA was found to be the most effective in suppressing both chain degradation and crosslinking side reactions. We also found that FAA and ECA could effectively suppress the chain degradation in the grafting system, but the grafting system had high gel contents and experienced severe crosslinking. St and DMAC had some effects on inhibiting crosslinking, but there was still small amount of crosslinking. The proposed mechanism is that DECA reacts first with HBPE macroradicals to form stable macroradicals when DECA is added to the grafting system. The latter then reacts (or copolymerizes) with MAH to form MAH-grafted HBPE. Because the formed stable macromolecules contain amide group, both the chain degradation and crosslinking side reactions are effectively suppressed.In general, in the presence of radical initiator, HDPE mainly experiences crosslinking, while polypropylene undergoes chain scission. LDPE and LLDPE have both reactions simultaneously occurring. HBPE is more or less similar to the low-density materials having simultaneous crosslinking and degradation. In the grafting studies, these side reactions need to be controlled. The current work elucidates the grafting mechanisms and provides practical guidance in this regard.

Controllable Preparation Of Branched Polyethylene With Different Microstructures Via Chain Transfer Ethylene Polymerization Catalyzed By Alpha-Diimine Ni Complex/Methylaluminoxane/Diethylzinc

Controllable preparation of branched polyethylene with different microstructures via chain transfer ethylene polymerization catalyzed by α-diimine Ni complex/methylaluminoxane/diethylzinc

Modulation of the microstructure of polyethylene from ethylene polymerization mediated by -Diimine Ni complex/MAO via chain transfer to ZnEt2 and temperature

ETHYLENE POLYMERIZATIONS CATALYZED BY Α-Diimine COMPLEXES WITH DIFFERENT SUBSTITUENTS ON LIGAND BACKBONE

Preparation of Polyethylene Elastomers with Increased High Molecular Weight and Nearly Perfect Strain Recovery by Steric Control of Asymmetric Α-Diimine Nickel Catalyst

UHMWPE with Short‐chain Branches Synthesized by Alkenyl Substituted Phenoxy–imine Catalysts in Ethylene Polymerization

GRAFTING OF MALEIC ANHYDRIDE ONTO HYPERBRANCHED POLYETHYLENE AND SUPPRESSION OF CHAIN DEGRADATION AND CROSSLINKING SIDE REACTIONS

Synthesis Of Branched Polyethylene By Ethylene Homopolymerization With A Novel (Alpha-Diimine) Nickel Complex In The Presence Of Methylaluminoxane

Controllable Preparation of Branched Polyolefins with Various Microstructural Units Via Chain-walking Ethylene and Pentene Polymerizations

Preparation Of Highly Branched Polyethylene Using (Alpha-Diimine) Nickel Complex Covalently Supported On Modified Sio2

Combination of 8‐aminoquinoline Nickel Dichloride and Cp2ZrCl2 Catalysts for Ethylene Polymerization

Synthesis and Characterization of Branched Polyethylene by Ethylene Homopolymerization with Monotitanocene and Modified Methylaluminoxane Catalysts

Novel (Α-Diimine)nickel Catalyst for Preparing Branched Polyethylene with Single Ethylene Monomer

Preparation of Highly Branched Polyolefins by Controlled Chain‐walking Olefin Polymerization

Synthesis of Branched Polyethylene with Novel Late Transition Metal Catalyst

Synthesis of highly branched polyethylene using para-benzhydryl substituted iminopyridyl Ni(II) and Pd(II) complexes

Synthesis Of Long-Chain-Branched Polyethylene By Ethylene Homopolymerization With A Novel Nickel(Ii) Alpha-Diimine Catalyst

Long-chain highly branched polyethylene prepared with binary alpha-diimine nickel/MAO catalysts

Synthesis of Branched Polyethylene by Ethylene Homopolymerization with Novel Mono-titanocene Catalysts

Branched Polyethylene Prepared Byin Situ Copolymerization of Ethylene with Monotitanocene and Modified Methylaluminoxane Catalyst

Synthesis Of Branched Polyethylene By In Situ Polymerization Of Ethylene With Combined Iron Catalyst And Ziegler-Natta Catalyst