ETHYLENE POLYMERIZATIONS CATALYZED BY Α-Diimine COMPLEXES WITH DIFFERENT SUBSTITUENTS ON LIGAND BACKBONE
Guo Chunwen,Fan Hong,Wang Wenjun,Li Bogeng
DOI: https://doi.org/10.3724/sp.j.1105.2009.00823
2009-01-01
Acta Polymerica Sinica
Abstract:Four alpha-diimine nickel complexes Ar-N=C(R-1) C(R-2)=N-ArNiBr2 with different alkyl substituents on backbone of ligand [Ar = 2, 6-dimethylphenyl, R-1 = C-n H2n+1, R-2 = C-m H2m+1; Cat 1 : m = 1, n = 1; Cat 2: m = 2, n = 1; Cat 3: m = 3, n = 1; Cat 4: m = 2, n = 2] were synthesized and used to catalyze ethylene polymerization in toluene. The influences arousing from changes in alkyl substituents on the backbone carbon of the catalyst ligand on the ethylene polymerization activities, microstructures and serni-crystalline properties of polyethylene were evaluated under varied polymerization temperatures and catalyst concentrations. It was showed that the catalysts with asymmetric alkyl substituents, i.e. R, and R, were different, had higher activity and produced polyethylenes having higher molecular weight as compared with those with symmetric substituents. With Cat 2 and Cat 3, the ethylene polymerization activities reached 1.86 x 10(3) kg PE/(mol Ni . h) and 1.92 x 10(3) kg PE/(mol Ni . h), and molecular weights of polymers achieved 68.2 x 10(4) and 101.9 x 10(4), respectively under the condition of 20 degrees C, atmosphere and 5.8 mmol/L of catalyst concentration. Analysis of polyethylene chain structures indicated that the main branching chain structure in polyethylene was methyl groups, and the branching degree was dependent mainly on polymerization temperature. Meanwhile, it was also showed that the polyethylene synthesized with alpha-diimine nickel complexes containing diversed alkyl substituents on ligand backbone had comparatively high proportion of hexyl and longer alkyl branching chains in polymer molecules, especially for the cases when polymerization was conducted at 40 degrees C.