n‐ZrS3/p‐ZrOS Photoanodes with NiOOH/FeOOH Oxygen Evolution Catalysts for Photoelectrochemical Water Oxidation
Zhangliu Tian,Meng Wang,Ganwen Chen,Jie Chen,Yumin Da,Hanqian Zhang,Rui Jiang,Yukun Xiao,Baihua Cui,Chonglai Jiang,Yishui Ding,Jinlin Yang,Zejun Sun,Cheng Han,Wei Chen
DOI: https://doi.org/10.1002/anie.202414209
2024-10-11
Angewandte Chemie International Edition
Abstract:Photoelectrochemical water splitting offers a promising approach for carbon neutrality, but its commercial prospects are still hampered by a lack of efficient and stable photoelectrodes with earth-abundant materials. Here, we report a strategy to construct an efficient photoanode with a coaxial nanobelt structure, comprising a buried-ZrS3/ZrOS n-p junction, for photoelectrochemical water splitting. The p-type ZrOS layer, formed on the surface of the n-type ZrS3 nanobelt through a pulsed-ozone-treatment method, acts as a hole collection layer for hole extraction and a protective layer to shield the photoanode from photocorrosion. The resulting ZrS3/ZrOS photoanode exhibits light harvesting with good photo-to-current efficiencies across the whole visible region to over 650 nm. By further employing NiOOH/FeOOH as the oxygen evolution reaction cocatalyst, the ZrS3/ZrOS/NiOOH/FeOOH photoanode yields a photocurrent density of ~9.3 mA cm-2 at 1.23 V versus the reversible hydrogen electrode with an applied bias photon-to-current efficiency of ~3.2% under simulated sunlight irradiation in an alkaline solution (pH = 13.6). The conformal ZrOS layer enables ZrS3/ZrOS/NiOOH/FeOOH photoanode operation over 1000 hours in an alkaline solution without obvious performance degradation. This study, offering a promising approach to fabricate efficient and durable photoelectrodes with earth-abundant materials, advances the frontiers of photoelectrochemical water splitting.
chemistry, multidisciplinary