Structure And Properties Of Melt-Spun Zn-Rich Zn-Mg Alloys

Hy Liu,Y Li,H Jones

1992-01-01

Abstract:Zinc together with five Zn-based alloys containing between 0.5 and 2.79 wt%Mg were rapidly solidified by melt spinning. For the alloys three kinds of microstructure were observed as-spun. Fine grained alphaZn equiaxed in cross section without or with Mg2Zn11 mainly along grain boundaries was found at the chill surface or just above the chill surface of the ribbon while coarser grained alphaZn with MgZn2 dispersoid in the alphaZn matrix was present at the free side of the ribbon. Addition of 0.5 wt%Mg to pure Zn gave rise to a 20-fold decrease in alphaZn grain section size at the chill side of the ribbon. Further addition of Mg up to 2.8 wt% gave a more gradual decrease in alphaZn grain section size. It was found that solid solubility of Mg in alphaZn was extended to 2.8 wt% at the chill surface of the ribbon. Heat treatment above 200-degrees-C resulted in rapid precipitation and growth of Mg2Zn11 in the alphaZn solid solution at the chill side of the ribbons while MgZn2 dissolved and Mg2Zn11 precipitated and grown in the alphaZn solid solution at the free side of the ribbons. Chill surface microhardness increased with alloy concentration and exhibited a Hall-Petch relationship with alphaZn grain size d according well with previous data on grain size hardening for pure Zn, Zn/ZnO and Zn-Ti-Cr.