Review On Methodologies Of Progressive Failure Analysis Of Composite Laminates

P. F. Liu,J. Y. Zheng

2010-01-01

Abstract:Stiffness degradation for laminated composites such as carbon fiber/epoxy composites is an important physical response to the damage and failure evolution under continuous or cyclic loads. The ability to predict the initial and subsequent evolution process of such damage phenomenon is essential to explore the mechanical properties of laminated composites. This chapter gives a general review on the popular methodologies which.deal with the damage initiation, stiffness degradation and final failure strength of composite laminates. These methodologies include the linear/nonlinear stress calculations, the failure criteria for initial microcracking, the stiffness degradation models and solution algorithms in the progressive failure analysis. It should be pointed out that the assumption of constant damage variable which is introduced into the constitutive equations of laminated composites to simulate the stiffness degradation properties is less effective and practical than that of changed damage variable with loads in the framework of continuum damage mechanics (CDM). Also, different damage evolution laws using CDM should be assumed to describe three failure modes: fiber breakage, matrix cracking and interfacial debonding, respectively.