Fatigue performance of 7475-T7351 aluminum alloy plate
CHEN Jun,DUAN Yu-lu,PENG Xiao-yan,XIAO Dan,XU Guo-fu,YIN Zhi-min
DOI: https://doi.org/10.19476/j.ysxb.1004.0609.2015.04.007
2015-01-01
The Chinese Journal of Nonferrous Metals
Abstract:The optical microscopy, orientation distribution function and scanning electron microscopy were used to investigate the fatigue properties and the rate of fatigue crack growth of 7475-T7351 alloy plate with thickness of 25 mm. The results show that the fatigue strength is anisotropic for the plate, it is 300 MPa along the transverse direction and 310 MPa along the longitudinal direction, respectively, and the fatigue life is longer than 1×107 cycle. Under the conditions of Kt=1, stress ratio R=0.1 and stress intensity factor amplitude ?K=30 MPa·m1/2, the fatigue crack growth rate da/dN along the longitudinal and transverse direction are 2.73×10?3?4.41×10?3 mm/cycle and 5.76×10?3?8.22×10?3 mm/cycle, respectively. The fatigue cracks mainly initiate on the non-metallic inclusions containing O, Na, Cl and coarse second phase on the sub-surface. A large number of striations are observed in the fatigue propagation zone, and a mixture of small dimples and cleavage is observed on the fracture surface in the fatigue fracture zone.