Abstract:The aim of this study was to investigate the influence of fineness and heat-treatment on the pozzolanic and engineering properties of volcanic ash. To this end, two different fineness levels of volcanic ash, ultra-fine (VAF) and fine (VA), without and after heat treatment at different temperatures (VA550, VA650, and VA750), were partially substituted for cement. In addition to the control (100% cement), five binary mortar mixes, each containing 20% of the different types of volcanic ash (VAF and VA; heat-treated and not), were prepared. First, X-ray fluorescence (XRF), X-ray powder diffraction (XRD), particle size analysis, and modified Chappelle tests were used to characterize the material. All mortar mixes were then tested for compressive strength development, water absorption, and apparent porosity. Finally, the microstructure of each of the mixes was evaluated by performing XRD, thermogravimetric analysis (TGA), and Fourier transform infrared spectroscopy (FTIR) analyses on paste samples at 91 days post-formation. The XRD and Chappelle reactivity results revealed increased pozzolanic reactivity with increasing volcanic ash fineness. In contrast, heat treatment adversely affected the pozzolanic reactivity of the volcanic ash due to the formation of crystalline phases at high temperatures. The mortars containing VAF20 (VAF, no heat, at 20%) showed slightly improved compressive strength (69.6 MPa) than the control (68.1 MPa) and all other binary mixes (66.7, 63.5, 64.2, and 63.9 MPa for VA20, VA20-550, VA20-650, and VA20-750, respectively) at 91 days. The mortar containing VAF20 demonstrated the lowest level of water absorption (9.3%) and apparent porosity (19.1%) of all mixes, including the control. The XRD results for the paste samples show that both VA and VAF showed the least intensity of portlandite phase, as compared to the control and other binary mixes. TGA results also show that binary mixes of VA and VAF have a reduced amount of portlandite, resulting in the densification of the mixes’ microstructures. With the addition of VAF, there is a significant shift in the FTIR band from 980 to 992 cm−1, which causes the formation of additional C–S–H gels that lead to the densification of the paste matrix. These results demonstrate that VAF exhibits high pozzolanic reactivity, making it suitable for use as a natural pozzolan that can partially substitute cement in the production of strong, durable, and environmentally friendly concrete.

Activation of Bagasse Ash in Cement Using Different Techniques

Chemical Activation of Bagasse Ash in Cement Mortar

Effect of different activation techniques on the engineering properties of cement-free binder containing volcanic ash and calcium carbide residue

Activation of Clay in Cement Mortar Applying Mechanical, Chemical and Thermal Techniques

Use of Bagasse Ash in Concrete and Its Impact on the Strength and Chloride Resistivity

The Effect of Mechanical Activation of Fly Ash on Cement-Based Materials Hydration and Hardened State Properties

Effective function of activated bagasse ash for high early strength geopolymer

Production of cleaner binders by reusing agricultural by-products: An approach towards zero cement concrete for sustainable future infrastructure

Potential of sugarcane bagasse ash as supplementary cementitious material and comparison with currently used rice husk ash

Sugarcane bagasse ash as supplementary cementitious material in cement composites: strength, durability, and microstructural analysis

Effect of Biochar and Sewage Sludge Ash as Partial Replacement for Cement in Cementitious Composites: Mechanical, and Durability Properties

Influence of Alkaline Activator on the Strength of Fly Ash-Cement Gel Sand Material

Reuse of Silica Rich Sugarcane Bagasse Ash in Concrete and Influence of Different Curing on the Performance of Concrete

Sugarcane bagasse ash as supplementary cementitious material in concrete- a review

Effect of activator concentration on setting time, workability and compressive strength of sustainable concrete with alkali-activated slag binder

To Study the Partial Replacement of Cement with Sugarcane Bagasse and Wood Ash with Addition of Aramid Fiber

Alkaline Activation of Binders: A Comparative Study

Effect of organic alkali on hydration of GGBS-FA blended cementitious material activated by sodium carbonate

Strength and Microstructural Characteristics of Activated Fly Ash–Cement Paste

Effect of Fineness and Heat Treatment on the Pozzolanic Activity of Natural Volcanic Ash for Its Utilization as Supplementary Cementitious Materials

Reuse of Uncontrolled Burnt Bagasse Ash from Sugar Industries with Waste Rubber Powder in Construction: A Waste to Wealth Approach for Sugar Mills