Abstract:3D flower-like Ni(OH)2 architectures including α- and β-Ni(OH)2 phases, respectively, have been successfully synthesized via a facile microwave-assisted hydrothermal method. The as-prepared samples were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM) and N2 adsorption, respectively. The possible mechanism of Ni(OH)2 architectures has been discussed and found that the reaction temperature plays a critical role in the formation of two kinds of products. Specifically, flower-like β-Ni(OH)2 with monolayer petals and α-Ni(OH)2 with bilayer petals were prepared at 120 °C and 150 °C, respectively. It was suggested that both architectures hold the advantages of large surface-exposure areas and can be readily separated for wastewater treatment due to their particular surface microstructures. Adsorption results showed that both samples exhibited significantly different selectivities for cationic/anionic dyes such as methylene blue (MB) and acid fuschine in aqueous solutions. The hydrophilic properties of two samples were investigated at room temperature. Furthermore, the relationships among the adsorption abilities, the hydrophilic properties and their applications in wastewater treatment of Ni(OH)2 architectures have been discussed in detail.

Synthesis And Characterization Of Beta-Ni(Oh)(2) Flower-Like Patterns

Size- and Structure-Controlled Synthesis and Characterization of Nickel Nanoparticles

Preparation and Test of Hierarchical Α-Ni(oh)<sub>2</sub> Flowers and Spheres

Synthesis of Alpha-Ni(Oh)(2) Peonies Assembled from Nanosheet Building Blocks and Corresponding Nio Porous Peonies

Synthesis, Characterization, and Magnetic Properties of Flower‐like Nickel Materials

Phase-controlled Synthesis of 3D Flower-Like Ni(OH)2 Architectures and Their Applications in Water Treatment

Morphology and Composition Controlled Synthesis of Flower-Like Silver Nanostructures.

Formation of Uniform Flowerlike Patterns of NiS by Macrocycle Polyamine Assisted Solution-Phase Route

Synthesis of Nickel Hydroxychloride Microspheres Via a Facile Template-Free Process and Their Conversion to Β-Ni(oh)2 Microspheres

Synthesis and Characterization of Ni(OH)2 Single-crystal Nanorods

Optimization of Hydrothermal Synthesis of Nickel Oxide with Flower-Like Structure

Aqueous solution route to flower-like microstructures of ferromagnetic nickel nanotips

Controlled Fabrication and Property Studies of Nickel Hydroxide and Nickel Oxidenanostructures

Hydrothermal Growth and Morphology Modification of Β-Nis Three-Dimensional Flowerlike Architectures

Simple Template-Free Solution Route for the Synthesis of Ni(SO4)0.3(OH)1.4nanobelts and Their Thermal Degradation

Experimental Study on Synthesis of Nio Nano-Particles

Nickel Flower-Like Nanostructures Composed of Nanoplates: One-Pot Synthesis, Stepwise Growth Mechanism and Enhanced Ferromagnetic Properties

Preparation and Characterization of Flowerlike Nickel Oxide

Synthesis and Characterization of Regular Hexagonal Nico2o4 Nanosheets

Bioinspired peony-like beta-Ni(OH)2 nanostructures with enhanced electrochemical activity and superhydrophobicity

Synthesis Of Single-Crystal Beta-Ni(Oh)(2) Nanodisks And Alpha-Fe2o3 Nanocrystals In C2h5oh-Naoh-Nh3 Center Dot H2o System