Abstract:The article discusses the results of the synthesis of spinel NiCo 2 O 4 by a new method of hydrothermolysis, as well as methods of precipitation of oxalates and ultrasonic aerosol pyrolysis from aqueous solutions of chlorides and nitrates of nickel and cobalt. The preparation conditions for each synthesis method were selected, the morphology of the obtained samples was considered, the porous structure of the material was studied, and the mesoporosity of the powders was estimated. Single-phase spinel NiCo 2 O 4 was obtained only by precipitation of oxalates; two other methods of synthesis, due to higher temperatures of the processes, lead to the appearance of an impurity of nickel–cobalt double oxide and a decrease in the nickel content in the spinel composition. The nature of the porosity of the materials obtained and the morphology depend on the synthesis method: the mesoporous structure in ultrasonic spray pyrolysis, macroporous structure in hydrothermolysis. The sample obtained by the oxalate precipitation method has the maximum specific surface area of 65.40 ± 0.33 m 2 /g and a pore volume of 0.409 cm 3 /g. The samples after hydrothermolysis have the minimum specific surface area of 10.22 ± 0.06 m 2 /g and a porosity of 0.055 cm 3 /g. The powders synthesized by ultrasonic spray pyrolysis have intermediate values of these characteristics between the other two methods, 41.68 ± 0.13 m 2 /g and 0.144 m 3 /g, respectively.

Synthesis and Characterization of Regular Hexagonal Nico2o4 Nanosheets

Experimental Study on Synthesis of Nio Nano-Particles

Synthesis of NiO nanowires by a sol-gel process

Studies on the nanocrystalline Co3O4 by wet synthesis and its microstructure

Influence of the synthesis method on the morphology, dispersion and porosity of nanostructured powders of nickel–cobalt spinel NiCo2O4

Gram‐scale Solvothermal Synthesis of Fe-doped CuCoO2 Nanosheets and Improvement of Oxygen Evolution Reaction Performance

Wet Chemical Synthesis And Magnetic Properties Of Core-Shell Nanocolumns Of Ni(Oh)(2)@Co(Oh)(2) And Their Oxides

Synthesis And Characterization Of Beta-Ni(Oh)(2) Flower-Like Patterns

Cobalt hydroxide nanosheets and their thermal decomposition to cobalt oxide nanorings.

Synthesis and electrochemical evaluation of nickel hydroxide nanosheets with phase transition to nickel oxide

A novel preparation method for NiCo<sub>2</sub>O<sub>4</sub> electrodes stacked with hexagonal nanosheets for water electrolysis

Effect of Precipitant on Preparation of Ni–Co Spinel Oxide by Coprecipitation Method

Synthesis, structural and optical properties of ZnO and Ni-doped ZnO hexagonal nanorods by Co-precipitation method

A Novel Preparation Method for NiCo2O4 Electrodes Stacked with Hexagonal Nanosheets for Water Electrolysis

A simple method to synthesize NiO fibers

Single-Nanometer Spinel with Precise Cation Distribution for Enhanced Oxygen Reduction

Synthesis of Nio Nanowires by an Oxidation Route

Preparation and characterization of NiO nanorods by thermal decomposition of NiC2O4 precursor

Synthesis and Characterisation of Core–Shell Microparticles Formed by Ni-Mn-Co Oxides

Effects of Co 2+ Doping on Physicochemical Behaviors of Hierarchical NiO Nanostructure

Synthesis and magnetic properties of NiS1 + x nanocrystallines