MoS2/CoCrNi Self-Lubricating Composite Coating and Its High-Temperature Tribological Properties

Liu Huiqiang,Cui Gongjun,Shi Ruibo,Li Sai,Kou Ziming

2020-01-01

Rare Metal Materials and Engineering

Abstract:The high-temperature self-lubricating CoCrNi-(3.0%, 5.0%, 7.0%) MoS2 (mass fraction) coatings were prepared on the surface of GH4169 alloy using powder metallurgy (P/M) technique. The high-temperature tribological properties of coatings sliding against Si3N4 ceramic ball were investigated by a ball-on-disk high-temperature tribo-meter. The effect of temperature, sliding speed and applied load on the tribological properties of coatings was studied from 20 degrees C to 800 degrees C. The phase and microstructure of the coatings were analyzed by X-ray diffractometer and scanning electron microscope, and the bonding strength between the coating and the substrate was tested through the thermal shock test. The results show that the MoS2 forms Mo2S3 and CrxSy phases with other metal elements. The coatings have a good interface structure with the substrate. The coatings consist of gamma(fcc), epsilon(hcp), CrxNiy and solid lubricating phases (Mo2S3, Cr-x,S-y). At low temperature, the friction coefficient of coatings gradually decreases with the increase of MoS2 content. At high temperature, the coatings have excellent high-temperature tribological properties. It is ascribed to the synergistic effect of chromate, oxide and sulfide on the wom surface. The wear rate of the coatings is below 5.5x10(-5) mm(3 center dot)N(-1 center dot)m(-1) over a wide temperature range, and the wear resistance of the coatings is 4 similar to 17 times higher than that of the substrate from 20 degrees C to 600 degrees C. The CoCrNi matrix coating with 5.0%MoS2 shows the best high-temperature tribological properties.