Optimization of a Novel Melt-Growth Heat Treatment of YbBa2Cu3O7-δ /ag Tapes

Zili Zhang,Jianyi Jiang,Qiuliang Wang,David C. Larbalestier,Eric E. Hellstrom

DOI: https://doi.org/10.1109/tasc.2018.2796385

IF: 1.9489

2018-01-01

IEEE Transactions on Applied Superconductivity

Abstract:A novel melt-growth heat treatment of YbBa 2 Cu 3 O 7-δ (Yb123) powder in Ag-sheathed tape has been established as a necessary first step to form aligned Yb123 grains in a powder-in-tube (PIT) conductor. The heat treatment parameters including the rate at which the atmosphere was changed from Ar to pure O 2, the heat treatment temperature, and the time during which the melt transformed back to Yb123 were investigated to find the optimum parameters for reforming Yb123 in Ag-sheathed tape. The Yb123 purity after being reformed is insensitive to the rate at which the atmosphere was changed. The optimized parameters are 910 °C for 48 h to reform Yb123.