A High-Efficiency and Energy-Saving Method for Purifying Industrial Silicon for Silicone Use
Yunfei He,Wenhui Ma,Aimin Xing,Pengbo Xu,Xi Yang
DOI: https://doi.org/10.1007/s12633-022-02141-4
IF: 3.4
2022-11-04
Silicon
Abstract:This study investigated an efficient method to reach a high yield of purified silicon crystals using solvent refining with directional solidification process(by applying a pulling out speed of 100μm/s). The main point is to add Sn in Al-Si melts during a 3kHz alternating electromagnetic field. The results show that the purified Si crystals can grow much bigger with Sn addition. When samples dealt in resistance with the Sn additions as 0, 10, 20, 30wt.%, the mean widths of Si crystals are 121.80, 303.45, 265.61, 244.19μm, respectively. While dealt in alternating electromagnetic furnace, the mean widths of the Si crystals are 144.75, 196.34, 250.86, 203.87μm, respectively. The XRD patterns show that no complex compounds formed in the systems, which means that the purified Si won't be contaminated by impurities. Moreover, when Sn addition is 30wt.%, with 100 μm/s, after alternating electromagnetic directional solidification (AEM-DS), the Si content of Si-rich area can reach 90.49wt.%, which is higher about 20wt.% than the sample without Sn addition. The pulling out speed used in our research is 100μm/s, which is much higher than the traditional pulling out speed (10μm/s order of magnitudes, reported in other works). This method can potentially reach energy saving and high yield to manufacture purified silicon.
materials science, multidisciplinary,chemistry, physical