Abstract:Nitrogen-enriched porous carbon has been a promising material for CO2 capture in the recent decades. To enhance the performance of CO2 adsorption, both an N-active site and the textural properties are crucial determinants. Herein, ultra-microporous carbon with N-active species was prepared using two synthesis procedures: 1) one-step carbonization of a polybenzoxazine (PBZ) precursor at 800 °C, and 2) the CO2 activation process at 900 °C. The activated porous carbon had the higher specific surface area (943 m2/g) and a total pore volume (0.51 cm3/g) compared to un-activated porous carbon (335 m2/g and 0.19 cm3/g, respectively). In addition, the presence of N-active species such as pyridine-N, secondary-N, pyridone-N, and oxide-N in the carbon structures could be clearly observed in the high-resolution XPS spectra. The CO2 adsorption measurement was performed at 30 and 50 °C under a wide range of pressures (1-7 bar). The maximum amount of CO2 uptake was ca. 3.59 mmol/g for the activated porous carbon operated at 30 °C and a CO2 pressure of 7 bar, which was due to the high specific surface area and the large micropore volume. Specifically, carbon with a 3D interconnected pore structure, derived from the sol-gel process of the PBZ precursor, exhibited good structural stability and consequently led to better absorption capability under the high atmospheric pressure of CO2. The enhanced CO2 adsorption capability for the as-prepared porous carbon was based on two mechanisms: physisorption as a result of textural properties and chemisorption as a result of the acid-base interaction between the basic N functionality and the acidic CO2 gas. All results suggested that ultra-microporous carbon with N-active species prepared from polybenzoxazine is a promising adsorbent for CO2 capture and storage, which can be used at a wide range of pressures and in many applications e.g. flue gas adsorption and natural gas production.

Enhance Pore Structure of Cyanobacteria-Based Porous Carbon by Polypropylene to Improve Adsorption Capacity of Methylene Blue.

Co-pyrolysis of cyanobacteria and plastics to synthesize porous carbon and its application in methylene blue adsorption

Porous ZnCl2-Activated Carbon from Shaddock Peel: Methylene Blue Adsorption Behavior

Facile Preparation of Porous Carbon Derived from Pomelo Peel for Efficient Adsorption of Methylene Blue

Sorghum-Waste-Derived High-Surface Area KOH-Activated Porous Carbon for Highly Efficient Methylene Blue and Pb(II) Removal.

Activated carbon prepared by co-pyrolysis of waste tobacco straw and waste LDPE mulch film: characterization and application for methylene blue removal

Porous carbon derived from waste corrugated paper with KOH-NaOH mixture and its adsorption property for methylene blue

Cordierite Reinforced Graphite Nanocomposite with Superior Adsorption Capacity Synthesized by In-Situ Carbon-Bed Pyrolysis Method

Solving two environmental problems simultaneously:Microporous carbon derived from mixed plastic waste for CO 2 capture

Facile synthesis of novel bi-heteroatom functionalized hyper-crosslinked porous polymers with efficient adsorption of methylene blue and methyl orange

Low-temperature Synthesized Hierarchical Porous Carbon from Waste Hydrochar with Super Capacity for Dye Adsorption

Efficient Removal of Methylene Blue from Aqueous Solutions Using a High Specific Surface Area Porous Carbon Derived from Soybean Dreg

Development and CO2 capture of nitrogen-enriched microporous carbon by coupling waste polyamides with lignocellulosic biomass

Enhanced CO2 capturing over ultra-microporous carbon with nitrogen-active species prepared using one-step carbonization of polybenzoxazine for a sustainable environment

Preparation of ZnO-Incorporated Porous Carbon Nanofibers and Adsorption Performance Investigation on Methylene Blue

Co-pyrolysis and activation of microalgae and waste polypropylene in the synthesis of nitrogen doped and porous carbon for pollutant adsorption

PDA@UiO-66-NH 2 -derived nitrogen and oxygen-doped hierarchical porous carbon for efficient adsorption of BPA and dyes

Integrated "adsorption-catalysis-adsorption" green strategy for efficient adsorption for the removal of methylene blue and catalytic preparation of hydrocarbon-rich, low N/O bio-oil

Organic salt-assisted pyrolysis for preparation of porous carbon from cellulose, hemicellulose and lignin: New insight from structure evolution

Hierarchically Porous Carbon Membranes Derived from Pan and Their Selective Adsorption of Organic Dyes

Structural control of a novel hierarchical porous carbon material and its adsorption properties