Multishelled Ni 2 P Microspheres as Multifunctional Sulfur Host 3D-Printed Cathode Materials Ensuring High Areal Capacity of Lithium–Sulfur Batteries
Fan Zhang,Zhi Li,Tong Cao,Kai Qin,Qunjie Xu,Haimei Liu,Yongyao Xia
DOI: https://doi.org/10.1021/acssuschemeng.1c01580
2021-04-22
Abstract:Lithium–sulfur (Li–S) batteries have higher theoretical capacity and higher energy density, so they are considered to be one of the most promising candidates for next-generation energy storage devices. However, electrolyte-soluble polysulfides cause a shuttle effect and lead to poor cycle stability. This is one of the main obstacles to the practical applications of LSB technology. To overcome this problem, here, we report polar Ni<sub>2</sub>P hollow microspheres, with multilayer nesting, as sulfur host materials. Specifically, the multilayer polar Ni<sub>2</sub>P can simultaneously act as a multilayer physical barrier and chemical adsorption material. In addition, the Ni<sub>2</sub>P microspheres serve as activation catalysts, accelerating the redox reaction kinetics. The above features allow the structure to effectively suppress the shuttle effect and improve the discharge capacity and cycle stability of LSB. For example, the three-dimensional printed Ni<sub>2</sub> (3DP-Ni<sub>2</sub>) cathode can provide an initial capacity of 682 mAh/g, obtaining high cycle stability with low-capacity attenuation of 0.0072% per cycle for 400 cycles under 2C. Even when the sulfur loading is increased from 6.1 to 9.3 mg/cm<sup>2</sup>, this material still shows good capacity retention. This work inspires the design of multifunctional cathode materials and paves a new path for the development of Li–S batteries.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acssuschemeng.1c01580?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acssuschemeng.1c01580</a>.XRD spectra of NiO; CV curves of the 3DP-Ni<sub>2</sub> and cathodes; charge and discharge curves with the 3DP-Ni<sub>2</sub> and cathodes; cycling performance of and 3DP-Ni<sub>2</sub> cathodes at 0.5C, 1C, and 2C; photograph of the pole piece; rheological properties of the printing ink; photograph of the 3D-printed sulfur cathodes and the simulated battery; XPS spectra of Ni 2p for Ni<sub>2</sub>P of Ni<sub>2</sub>P-Li<sub>2</sub>S<sub>6</sub>; Li<sub>2</sub>S<sub>6</sub> symmetrical cell with the Ni<sub>2</sub>P electrode; minimum energy path and potential energy profiles for Li ion diffusion on the Ni<sub>2</sub>P (111) facet, (210) facet, (111) facet, and carbon black surface; and table of comparison of the performances at high sulfur loading conditions (<a class="ext-link" href="/doi/suppl/10.1021/acssuschemeng.1c01580/suppl_file/sc1c01580_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
chemistry, multidisciplinary,engineering, chemical,green & sustainable science & technology